Composite self-cohered web materials

ABSTRACT

The present invention is directed to implantable bioabsorbable non-woven self-cohered web materials having a high degree of porosity. The web materials are very supple and soft, while exhibiting proportionally increased mechanical strength in one or more directions. The web materials often possess a high degree of loft. The web materials can be formed into a variety of shapes and forms suitable for use as implantable medical devices or components thereof.

CROSS-REFERENCE TO RELATED APPLICATIONS

This is a continuation application of application Ser. No. 11/193,086filed Jul. 29, 2005 now abandoned.

FIELD OF THE INVENTION

The present invention relates to implantable medical materials anddevices. More particularly, the present invention is directed toimplantable medical materials and devices made with bioabsorbablepolymeric materials in the form of non-woven, self-cohered, filamentouswebs having a high degree of porosity.

BACKGROUND OF THE INVENTION

A variety of bioabsorbable polymeric compounds have been developed foruse in medical applications. Materials made from these compounds can beused to construct implantable devices that do not remain permanently inthe body of an implant recipient. Bioabsorbable materials are removedfrom the body of an implant recipient by inherent physiological processof the implant recipient. These processes can include simple dissolutionof all or part of the bioabsorbable compound, hydrolysis of labilechemical bonds in the bioabsorbable compound, enzymatic action, and/orsurface erosion of the material. The breakdown products of theseprocesses are usually eliminated from the implant recipient throughaction of the lungs, liver, and/or kidneys. It is recognized that in theliterature “bioresorbable,” “resorbable,” “bioabsorbable,” and“biodegradable” are terms frequently used interchangeably.“Bioabsorbable” is the preferred term herein.

Bioabsorbable polymeric compounds have been used in wound closure andreconstruction applications for many decades. Sutures are the mostnotable examples. Molded articles, films, foams, laminates, woven, andnon-woven materials have also been produced with bioabsorbable polymericcompounds. Biologically active compositions have been releasablycombined with some of these bioabsorbable compounds.

U.S. Pat. No. 6,165,217, issued to Hayes, discloses a bioabsorbablematerial in the form of a non-woven self-cohered web (FIGS. 1 and 1A,herein). A self-cohered non-woven web material is a spun web ofcontinuous filaments made of at least one semi-crystalline polymericcomponent covalently bonded as a linear block copolymer with or blendedwith one or more semi-crystalline or amorphous polymeric components.

The continuous filaments are produced by selecting spinning conditionsthat provide a tackiness to the emerging filaments and allows them toself-cohere as solid filaments as the filaments are collected in acohesive random pile, or web, on a collecting surface. The spunfilaments are intermingled together as they are collected in the form ofa porous web of self-cohered filaments. The self-cohered filaments havemultiple contact points with each other within the web. The self-coheredfilaments bond at the contact points without need for requisite additionof supplementary adhesives, binders, adhesive adjuncts (e.g., solvents,tackifier resins, softening agents), or post extrusion melt processing.The self-cohered filaments of the preferred embodimentpolyglycolide:trimethylene carbonate (PGA:TMC) non-woven web are between20 microns and 50 microns in diameter. According to Hayes, theseself-cohered non-woven webs possess volume densities (also reported asapparent densities) that indicate percent porosity to be in a rangebetween approximately forty (40) and eighty (80). If the potentiallysemi-crystalline web is preserved in a thermodynamically unstable(metastable), homogeneous (microphase disordered), substantially phasemiscible, amorphous state of limited crystallinity, the web is malleableand can be ready conformed or molded into a desired shape. That shapedform can then be preserved through its conversion into a more ordered,thermodynamically stable, at least partially phase immisciblesemi-crystalline state. This irreversible (short of complete remeltingand reformation of the formed web structures) conversion from aprolonged amorphous (i.e., disordered state of miscibility) conditioninto an ordered semi-crystalline state is typically provided by thechain mobility present in the rubbery state existing between the melttemperature and that of the order-disorder transition temperature(T_(odt)), the temperature above which the transition from disorder toorder can proceed. Alternatively, solvents, lubricants, or plasticizingagents, with or without their combination with heat, can be used tofacilitate chain mobility, and rearrangement of the constituent polymerchains into a more ordered condition. The chemical composition of theself-cohered filaments can be chosen so the resultant web is implantableand bioabsorbable.

Hayes describes the self-cohered non-woven web material as possessing adegree of porosity variable based on fiber deposition density and anysubsequent compression. Hayes also describes the ability of the planarweb in the malleable unstable amorphous condition to be shaped into avirtually unlimited array of forms, the shapes of which can be retainedthrough subsequent crystallization. However, Hayes does not indicate anunset web of the self-cohered filaments which can serve as a precursorweb material for additional stretch processing to increase web porosityprior to annealing. Nor does Hayes teach a self-cohered non-woven webmaterial having a significant population of continuous filaments with across-sectional diameter less than twenty (20) microns. In the absenceof additional processing of a precursor web material according to thepresent invention, the self-cohered non-woven web material of Hayeswould not have increased molecular orientation in the self-coheredfilaments of the web sufficient to provide a birefringence value greaterthan 0.050.

A non-woven self-cohered web material having high porosity and smallfilament diameter would have proportionally increased mechanicalstrength in one or more directions. Despite increased mechanicalstrength, such a high porosity non-woven self-cohered web material woulddeliver more loft, suppleness, drapability, conformability, and tissuecompliance than a web material made according to Hayes.

For non-implantable applications, a non-woven self-cohered web having ahigh degree of porosity could be used to releasably attach implantabledevices and materials to a delivery apparatus. Combining a population oforiented filaments with an increased internal void volume within whichthe oriented filament can move would imbue such a material with a degreeof elasticity or resiliency.

In addition to these and other improvements in such a web material, amore porous bioabsorbable web material would provide opportunities tocombine other components with the web. The components could be placed onsurfaces of the filaments. The components could also be placed withinvoid spaces, or pores, between the filaments. The components could bebioabsorbable or non-bioabsorbable. The components, in turn, couldreleasably contain useful substances.

There is a need, therefore, for a synthetic bioabsorbable, non-woven,self-cohered polymeric web material having a high degree of porositywith increased mechanical strength, loft, suppleness, drapability,comformability, and tissue compliance.

SUMMARY OF THE INVENTION

The present invention is directed to synthetic bioabsorbable, non-woven,self-cohered polymeric web materials having a high degree of porosity.The highly porous web materials are mechanically strong and have a highdegree of loft, suppleness, drapability, conformability, and tissuecompliance. In some embodiments, the present invention exhibits elasticproperties. The invention is suitable for use as an implantable medicaldevice or a component of a medical device. The invention is alsosuitable for use in many instances as a thrombogenic agent at a site ofbleeding or aneurysm formation.

These properties are imparted to the present invention by drawing, orstretching, an unannealed, self-cohered, precursor web material in atleast one direction at a particular rate and stretch ratio under definedconditions. Stretching is followed preferentially by heat-setting andcooling under full or partial restraint.

Self-cohered, precursor web materials have filaments attached to oneanother at multiple contact points (FIGS. 1 and 1A). During processing,the filaments are kept secured together by the self-cohering contactpoints. As the self-cohered filaments are stretched, the filamentselongate and become smaller in cross-sectional diameter (FIGS. 2-4A, and6-7). As the filaments become finer, increased void space is formedbetween the filaments (Table 12). The as-stretched structure is then“set” or annealed, either completely or partially under restraint, toinduce at least partial phase immiscibility and subsequentcrystallization. The finer filaments and increased void space generatedwithin the web material are responsible for many of the improvedcharacteristics of the present invention.

A convenient metric for quantifying the void space of a porous webmaterial is the percent porosity of the finished web material. Thepercent porosity compares the density of an unprocessed startingcompound with the density of a finished porous web material. Thestretched, self-cohered, continuous filament nonwoven web materials ofthe present invention are greater than ninety percent (90%) porous. Inthe present invention, the increased porosity imparted to the web isdefined as the void space provided within the external boundaries of thestretched self-cohering web, absent the inclusion of any fillers orother added components that may effectively reduce the availableporosity.

The present invention can include additional compositions placed onand/or within the polymeric components of the web material. Additionalcompositions can also be placed in void spaces, or pores, of the webmaterial. The compositions can include useful substances releasablycontained thereby. Preferred compositions for placement in void spacesand surfaces of the present invention are hydrogel-based materials.

In one embodiment, the present invention is an implantable articlecomprising melt-formed continuous filaments intermingled to form aporous web wherein said filaments are self-cohered to each other atmultiple contact points, wherein said filaments comprise at least onesemi-crystalline polymeric component covalently bonded to or blendedwith at least one amorphous polymeric component, wherein the filamentspossess partial to full polymeric component phase immiscibility when ina crystalline state, wherein said implantable article has a percentporosity greater than ninety in the absence of additional components,and wherein said implantable article is in the form of a hollow tube.

In another embodiment, the present invention is n implantable articlecomprising melt-formed continuous filaments intermingled to form aporous web wherein said filaments are self-cohered to each other atmultiple contact points, wherein said filaments comprise a firstsemi-crystalline polymeric component covalently bonded to or blendedwith at least one additional semi-crystalline polymeric component,wherein the filaments possess partial to full polymeric component phaseimmiscibility when in a crystalline state, wherein said implantablearticle has a percent porosity greater than ninety in the absence ofadditional components, and wherein said implantable article is in theform of a hollow tube.

These and other features of the present invention, as well as theinvention itself, will be more fully appreciated from the drawings anddetailed description of the invention.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a scanning electron micrograph (SEM) of a self-cohered webmaterial of the prior art.

FIG. 1A is a scanning electron micrograph (SEM) of a self-cohered webmaterial of the prior art.

FIG. 2 is a 50× scanning electron micrograph (SEM) of an embodiment ofthe present invention having been stretched in a single direction.

FIG. 2A is a 100× scanning electron micrograph (SEM) of an embodiment ofthe present invention having been stretched in a single direction andconstructed from 50-50 PGA:TMC.

FIG. 3 is a scanning electron micrograph (SEM) of an embodiment of thepresent invention having been stretched in two directions substantiallyperpendicular to each other.

FIG. 4 is a scanning electron micrograph (SEM) of an embodiment of thepresent invention having a form referred to herein as fleece.

FIG. 4A is a scanning electron micrograph (SEM) of an embodiment of thepresent invention having been stretched in all directions outwardly fromthe center of the material.

FIG. 5 is a schematic illustration of an apparatus suitable to produce aprecursor web material for use in the present invention.

FIG. 6 is a graph showing the effect of different stretching ratios onthe diameter of the filaments in the finish web material of the presentinvention.

FIG. 7 is a graph showing the percentage of filaments having a diameterless than twenty (20) microns for a given stretching ratio.

FIG. 8 is a graph showing the relationship of birefringence to filamentdiameter in a finished web material of the present invention.

FIG. 9 in an illustration of a web material of the present inventionhaving at least one additional material placed on surfaces and in voidspaces of the web material.

FIG. 9A is an illustration of a web material of the present inventionhaving at least two additional materials placed on surfaces and in voidspaces of the web material.

FIG. 10 is an illustration of a web material of the present inventionattached to a pledget material.

FIG. 10A is an illustration of a web material of the present inventionattached to a pledget material and placed on a stapling apparatus.

FIG. 10B is an illustration of a web material of the present inventionattached to a pledget material and placed on a stapling apparatus.

FIG. 11 is an illustration of a web material of the present invention inthe form of an anastomotic wrap.

FIG. 12 is an illustration of a web material of the present inventionplaced between a second material having openings therein through whichthe web material is exposed.

FIG. 13 is an illustration of a web material of the present inventionhaving a tubular form.

FIG. 14 is an illustration of a web material of the present inventionhaving a cylindrical form.

FIG. 15 is an illustration of a web material of the present inventionand a non-bioabsorbable material.

FIG. 16 is an illustration of a web material of the present invention ina tubular form with at least one structural element included therewith.

FIG. 17 is an illustration of a web material of the present invention ina tubular form having an ability to change dimension radially andlongitudinally.

FIG. 18 is an Illustration of a whole blood coagulation time assay.

FIG. 19 is a photograph of a web material of the present inventionhaving a very high degree of porosity.

FIG. 19A is a photograph of a web material of the present inventionhaving a very high degree of porosity and a metallic band attachedthereto.

FIG. 19B is a photograph of a web material of the present inventionhaving a very high degree of porosity with multiple metallic bandsattached thereto.

FIG. 20 is an illustration of the web material of FIG. 19 placed insidea delivery device.

FIG. 21 is an illustration of a composite material having a stretchedself-cohered web material layered on a non-bioabsorbable material.

FIG. 21A is an illustration of a composite material having a stretchedself-cohered web material having a bioactive species releasablycontained therein layered on a non-bioabsorbable material.

DETAILED DESCRIPTION OF THE INVENTION

The present invention is directed to bioabsorbable non-woven,self-cohered, polymeric web materials having a high degree of porosity.The high degree of porosity imparts many desirable features to theinvention. These features include loft, suppleness, drapability,conformability, and tissue compliance. Many of these highly porousmaterials exhibit substantial mechanical strength. The highly porous webmaterials of the present invention can be used as implantable medicaldevices or components thereof. When implanted, the highly porousbioabsorbable web materials of the present invention are removed fromthe body of an implant recipient by inherent physiological processes ofthe implant recipient.

The highly porous web materials of the present invention are made bystretching an unannealed, non-woven, self-cohered, unstretched precursorweb material in one or more directions, sequentially or simultaneously,followed by annealing of the polymeric constituents of the stretched webmaterial with heat and/or appropriate solvents. The precursor webmaterial is made of continuous filaments formed from semi-crystallinemulti-component polymeric systems which, upon the achievement of anequilibrium state, possess some evidence of phase immiscibility of thesystem's constituent polymeric components. The ability of the precursorweb material to initially self-cohere after solidification from the meltis believed to be the result of a comparatively reduced rate ofcrystallization. The reduced rate of crystallization preserves themelt's substantially homogenous amorphous non-crystalline phase mixedcondition within the solidified quenched filamentous web until such atime that it can come into physical contact with other portions of thecontinuous filament sustained in a similar amorphous condition oflimited crystallization. As portions of the continuous filaments contacteach other at multiple points in the precursor web material, thefilaments are bonded together at the contact points in a solidifiedstate without requisite for added adhesive binders, adjuncts, or postextrusion melt processing. Continuous or discontinuous filamentsconnected in such a manner are considered to be “self-cohered.”

Blend and copolymeric systems that exist in a state of full componentmiscibility within their amorphous phase, be it in a metastable orequilibrium state, are expected to display a single T_(g) or T_(odt)occurring at a temperature that is a function of the systems'composition and substantially predictable when utilizing the Foxequation. Conversely, fully immiscible multiphase amorphous systems areexpected to display distinct T_(g)'s which correlate with thehomopolymer analogs for each separated immiscible phase. In a partiallymiscible system, some crystallizable or other constituents remainmiscible within the existing amorphous phase due to reasons such assteric constraints or segment inclusions. As a result, the respectiveT_(g) would be shifted away from that of its non-crystallizinghomopolymer analog toward a temperature reflective of the constituentratio existing within the amorphous phase, a value which could beinterpreted utilizing the Fox equation.

Similarly, non-crystallizing or amorphous inclusions within thecrystalline regions of such partially miscible systems, when present insufficient concentrations, can be expected to produce a diluent orcolligative effect resulting in a depression of the melting temperaturefrom that expected of a crystallized homopolymer analog. Such partiallymiscible systems would result in the depression of the observed T_(m)while a fully phase separated system would retain a T_(m) similar tothat of the homopolymer analog.

In the present invention, the self-cohered precursor web material can besuspended in a substantially homogenous amorphous non-crystallinemetastable phase mixed condition that enables the precursor web materialto be stretched in one or more directions, either sequentially orsimultaneously, to cause elongation and thinning of the self-coheredfilaments. Stretching a precursor web material increases void spacebetween the intermingled filaments in the web material. Though Hayesdescribes materials with a porosity between approximately forty andeighty percent for a finished self-cohered web made according to theteachings of U.S. Pat. No. 6,165,217, the present inventors havediscovered the precursor web material can have void spaces amounting toninety-percent (90%) of the total volume of material. This metric isexpressed herein as a percent porosity, or simply “porosity.” Porosityis determined as described in Example 3, herein. Finished web materialsof the present invention have porosity values greater than ninetypercent (90%) (Table 12).

The prolonged amorphous state present in the precursor web materialduring processing is attainable through the preferential selection andutilization of at least partially phase immiscible blends or blockcopolymers combined with a sufficiently rapid rate of cooling thatsubstantially inhibits both full or partial microphase separation, aswell as subsequent crystallization. At least partially phase immiscibleblends of polymers or copolymers can be utilized, provided the polymericmixture possesses sufficient melt miscibility to allow for its extrusioninto filaments. The present invention preferentially utilizes blockcopolymers that can be described as diblock, triblock, or multiblockcopolymers that possess at least partially phase immiscible segmentalcomponents when in a thermodynamically stable state. Phase immiscibilityin the context of block copolymers is intended to refer to segmentalcomponents which, if a part of a blend of the correlating homopolymers,would be expected to phase separate within the melt.

More particularly, the current invention preferentially utilizes an ABAtriblock copolymer system synthesized through a sequential addition ringopening polymerization and composed of poly(glycolide), also known asPGA, and poly(trimethylene carbonate), also known as TMC, to form ahighly porous, stretched, self-cohered, non-woven bioabsorbable webmaterial; wherein A comprises between 40 and 85 weight percent of thetotal weight, and wherein A is comprised of glycolide recurring units;and B comprises the remainder of the total weight and is comprised oftrimethylene carbonate recurring units said material being bioabsorbableand implantable. Preferred precursor web materials are made with PGA:TMCtriblock copolymers having ratios of PGA to TMC of sixty-seven percent(67%) to thirty three percent (33%) (67:33-PGA:TMC) and fifty percent(50%) PGA to fifty percent (50%) TMC (50:50-PGA:TMC). The inherentviscosity of these polymers at 30° C. in hexafluoroisopropanol (HFIP),can range from an average of 0.5 dl/g to over 1.5 dl/g, and forpreferred use can range from 1.0 dl/g to 1.2 dl/g. The acceptablemelting point for this particular range of copolymer compositions asdetermined through a DSC melt peak can range from approximately 170° C.to 220° C. These copolymers' cumulative thermal exposure over time, beit from extrusion or other processing, needs to be minimizedsufficiently to prevent transesterification reactions that can result indegradation of the copolymers' block structure and their correlatingcrystallinity and phase immiscibility characteristics.

Once a self-cohered, continuous filament precursor web material has beenprepared as described herein, the web material is restrained andpre-heated above its order-disorder transition temperature (T_(odt)) andbelow its melting temperature (T_(m)) for a period of time sufficient tosoften the material without inducing significant crystallization. Thesoftened precursor web material is then subjected to stretching in oneor more directions (FIGS. 2-4A). Stretching the web material in multipledirections can be performed sequentially or in a single operation. Theprecursor web material is stretched at a particular rate and at aparticular ratio of initial dimension to final dimension.

In most uni-axially stretched embodiments (FIGS. 2 and 2A), theprecursor web material is stretched at rates preferably ten to fiftypercent (10-50%) of the precursor web initial dimensions per second. Fora given stretch rate, a precursor web material can be stretched at aratio between two to one (2:1) and eleven to one (11:1). Preferredratios are four to one (4:1), five to one (5:1), six to one (6:1), sevento one (7:1), eight to one (8:1), nine to one (9:1), and ten to one(10:1). Following stretching, the precursor web material is subjected toa heating step to anneal the polymeric material to induce partial tofull phase separation and subsequent crystallization. The annealing stepcan be preformed by one of two methods.

The first annealing method requires the web be maintained at the maximumstretch at annealing conditions until the web is nearly or fullyannealed. Preferred annealing conditions are 110° C. to 130° C. for 0.5to 3 minutes, although temperatures above the order-disorder temperature(T_(odt)) and below the melt temperature (T_(m)), with the appropriatetime adjustments, could be used.

The second annealing method is referred to herein as “partiallyrestrained.” In the method, the stretched self-cohered web material isfirst partially annealed while restrained at the maximum stretch. Theannealing step is then completed with the restraint on the stretched webmaterial reduced or eliminated. Preferred conditions for this method are70° C. for 0.5 minutes for the first step (full restraint) and 120° C.for 1 to 2 minutes for the final step (reduced or no restraint).

Once annealed, the highly porous self-cohered web material is removedfrom the processing apparatus and prepared for use as an implantablemedical device or component thereof. The advantage of the partiallyrestrained annealing method is that it allows the stretched web toretract, typically ten to sixty percent, without an increase in fiberdiameter or a reduction in porosity (see e.g., Example 9, infra)resulting in is a softer web. This softness is imparted by the curlingof the fibers in the web as they retract during the final annealingstep.

In most biaxially stretched embodiments (FIG. 3), the precursor webmaterial is stretched at an approximate rate of twenty percent (20%) orthirty percent (30%) per second at 25° C. to 75° C. One preferred methodis to stretch a precursor web material of 40 to 50 mg/cm² area weight at70° C. to a stretch ratio of 3.5:1 along the x-axis (down-web) and 6.0:1along the y-axis (transverse). By multiplying the stretch ratios of thex and y axis, this gives an area ratio of 21:1. The stretched web ispartially annealed at 70° C. for 2 minutes, then released fromrestraints and fully annealed at 120° C. for 2 minutes. Either annealingmethod described above may be used for annealing biaxially stretchedwebs.

Similar conditions are used for radially stretched precursor webmaterials (FIG. 4A). A radial stretch ratio of 3.75:1 (area ratio of14:1) is preferred, although a stretch ration of 4.5:1 (area ratio of20:1) works well. As in uniaxial and biaxial stretched webs, eitherannealing method described above may be employed.

Highly porous stretched self-cohered web materials of the presentinvention can be combined with one another to form layered or laminatedmaterials. Optionally, the materials can be further processed with heat,binders, adhesives and/or solvents to attach the individual layerstogether. Alternatively, portions of one or more of the layers canremain unattached and separated to form a space between the layers.

In some embodiments, highly porous stretched self-cohered web materialscan be made in the form of a rod, cylinder (FIG. 14), rope, or tube(FIG. 13). The tubular form can be made in a “stretchy” form that canelongate and/or increase in diameter (FIG. 17). These and other formscan be adapted for use with a particular anatomical structure orsurgical procedure. For example, a highly porous stretched self-coheredweb material in the form of a sheet can be adapted for placement aroundan anastomotic junction and sutured or stapled in place (FIG. 11). Inanother embodiment (FIG. 10), a pledget material (14) is combined with a“stretchy” form of the present invention (12) to effect a substantiallytubular structure (10) adapted to facilitate temporary placement of thepledget component onto a stapling apparatus cartridge (FIGS. 10A-10B).Alternatively, the present invention can additionally serve as thepledget component.

In addition, a highly porous stretched self-cohered web material of thepresent invention can be combined with other materials to form compositedevices (FIG. 15). In one embodiment, a sheet of stretched self-coheredbioabsorbable web material (28) is provided with a planarnon-bioabsorbable material (26) surrounding the web material to form adental implant (25). When implanted, bone or other tissue is encouragedto grow in a space defined by the implant. With time, the bioabsorbableweb material is removed from the implantation site by naturalphysiological processes of the implant recipient while bone or othertissue ingrows and fills the space. Once the bioabsorbable portion ofthe implant has disappeared, another dental implant can be placed at theregenerated bone or tissue present at the site exposed by thebioabsorbed web material of the present invention. An alternativeembodiment is illustrated in FIG. 12.

In another embodiment, a highly porous stretched self-cohered webmaterial (22) of the present invention is layered, and optionallylaminated, to a sheet of non-bioabsorbable material (24). This compositematerial (21) is particularly suited for use as a dura substitute incranial surgery (FIG. 21). Preferred non-bioabsorbable materials arefluoropolymeric in composition, with porous expandedpolytetrafluoroethylene (ePTFE) and/or fluorinated ethylene propylene(FEP) being most preferred. Bioactive substances (27) can be placed inor on the highly porous stretched self-cohered web material of thepresent invention (FIG. 21A).

In other embodiments (FIG. 16), structural elements (39) are combinedwith a highly porous stretched self-cohered web material (38) to form acomposite construction (36). The structural elements can be made ofnon-bioabsorbable and/or bioabsorbable materials. The structuralelements can be placed on one or both sides of the stretchedself-cohered web material. The structural elements can also be placedwithin the web material.

The high porosity of stretched self-cohered web materials of the presentinvention can be increased further by subjecting the web material to aprocedure that pulls the filaments apart to an even greater extent. Theprocedure may also fracture the continuous filaments of the stretchedweb material into pieces. These very porous stretched self-cohered webmaterials of the present invention have been shown to have highlythrombogenic properties. In a preferred form, the web material (49) hasthe appearance of a “cotton ball” (FIG. 19). One or more of thesereversibly compressible “thrombogenic cotton balls” (49) can be combinedwith a delivery system (48), such as a catheter, for implantation at asite of bleeding or aneurysm formation (FIG. 20). Additional elements,such as metallic bands (FIGS. 19A-B), can be added to the very highlyporous stretched self-cohered web material as visualization aids ormechanical supports. When used as a component for a medical device,these very highly porous, thrombogenic web materials can provide a sealbetween the device and surrounding anatomical structures and tissues.

Various chemical components (23) can be combined with the highly porousweb stretched self-cohered web materials (20) of the present invention(FIG. 9). The chemical components can be placed on surfaces of thepolymeric material comprising the highly porous web material. Thechemical components can also be placed in void spaces, or pores, of theweb material. The chemical compositions can be suitably viscous chemicalcompositions, such as a hydrogel material. Biologically activesubstances (27) can be combined with the additional chemical component(FIG. 9A). With hydrogel materials, for example, the biologically activesubstances can be released directly from the hydrogel material orreleased as the hydrogel material and the underlying web material arebioabsorbed by the body of an implant recipient. Preferred chemicalcomponents are in the form of hydrogel materials.

Suitable hydrogel materials include, but are not limited to, polyvinylalcohol, polyethylene glycol, polypropylene glycol, dextran, agarose,alginate, carboxymethylcellulose, hyaluronic acid, polyacrylamide,polyglycidol, poly(vinyl alcohol-co-ethylene),poly(ethyleneglycol-co-propyleneglycol), poly(vinyl acetate-co-vinylalcohol), poly(tetrafluoroethylene-co-vinyl alcohol),poly(acrylonitrile-co-acrylamide), poly(acrylonitrile-co-acrylicacid-acrylamidine), poly(acrylonitrile-co-acrylic acid-co-acrylamidine),polyacrylic acid, poly-lysine, polyethyleneimine, polyvinyl pyrrolidone,polyhydroxyethylmethacrylate, polysulfone, mercaptosilane, aminosilane,hydroxylsilane, polyallylamine, polyaminoethylmethacrylate,polyornithine, polyaminoacrylamide, polyacrolein, acryloxysuccinimide,or their copolymers, either alone or in combination. Suitable solventsfor dissolving the hydrophilic polymers include, but are not limited to,water, alcohols, dioxane, dimethylformamide, tetrahydrofuran, andacetonitrile, etc.

Optionally, the compositions can be chemically altered after beingcombined with the web material. These chemical alterations can bechemically reactive groups that interact with polymeric constituents ofthe web material or with chemically reactive groups on the compositionsthemselves. The chemical alterations to these compositions can serve asattachment sites for chemically bonding yet other chemical compositions,such as biologically active substances (27). These “bioactivesubstances” include enzymes, organic catalysts, ribozymes,organometallics, proteins, glycoproteins, peptides, polyamino acids,antibodies, nucleic acids, steroidal molecules, antibiotics,antimycotics, cytokines, carbohydrates, oleophobics, lipids,extracellular matrix material and/or its individual components,pharmaceuticals, and therapeutics. A preferred chemically-basedbioactive substance is dexamethasone. Cells, such as, mammalian cells,reptilian cells, amphibian cells, avian cells, insect cells, planktoniccells, cells from non-mammalian marine vertebrates and invertebrates,plant cells, microbial cells, protists, genetically engineered cells,and organelles, such as mitochondria, are also bioactive substances. Inaddition, non-cellular biological entities, such as viruses, virenos,and prions are considered bioactive substances.

The following examples are included for purposes of illustrating certainaspects of the present invention and should not be construed aslimiting.

EXAMPLES Example 1

This example describes formation of an article of the present invention.Initially, an unannealed, non-woven, self-cohered polymeric precursorweb was formed. The precursor web material was heated slightly andsubjected to stretching in a single, or uniaxial, direction to increasethe porosity of the web material. The highly porous self-cohered webmaterial was then set with heat.

The precursor web material was formed from a 67% poly(glycolide) and 33%poly(trimethylenecarbonate) (w/w) segmented triblock copolymer (67%PGA:33% TMC). The copolymer is available in resin form from UnitedStates Surgical (Norwalk, Conn., US), a unit of Tyco Healthcare GroupLP. This polymer is commonly referred to as polyglyconate and hashistorically been available through the former Davis & Geck (Danbury,Conn.). A typical 67% PGA:33% TMC resin lot was characterized previouslyby Hayes in U.S. Pat. No. 6,165,217, which is incorporated herein byreference. The process of characterizing the “67:33-PGA:TMC” resinmaterial is reiterated herein.

Approximately 25 mg of the acquired copolymer was dissolved in 25 ml ofhexafluoroisopropanol (HFIP). The dilute solution thus produced had aninherent viscosity (IV) of 1.53 dl/g as measured with a Cannon-Ubeloddeviscometer immersed in a water bath set at 30° C. (+/−0.05° C.).

Approximately 10 mg of the acquired copolymer was placed into analuminum differential scanning calorimetry (DSC) sample pan, covered,and analyzed utilizing a Perkin-Elmer DSC 7 equipped with an IntracoolerII cooling unit able to provide sample cooling to temperatures as low asminus forty degrees centigrade (−40° C.). After preconditioning of thesample at 180° C. for 2 minutes, the sample was cooled at the maximumrate provided by the instrument (−500° C./min setting) and scanned fromminus forty degrees centigrade (−40° C.) to two hundred fifty degreecentigrade (250° C.) at a scanning rate of 10° C./min. After completionof this initial scan, the sample was immediately cooled at the maximumrate provided by the instrument (−500° C./min setting). A second similarscan was undertaken on the same sample over the same temperature range.After scan completion and thermal maintenance at 250° C. for 5 minutes,the sample was again cooled at the maximum rate provided by theinstrument and a third scan undertaken.

Each scan was analyzed for the observed glass transition temperature(T_(g)), order-disorder transition temperature (T_(odt)),crystallization exotherm, and melt endotherm. The results are summarizedin Table 1.

TABLE 1 Exotherm Exotherm Melt T_(g)/T_(odt) T_(g)/T_(odt) Peak EnthalpyMelt Peak Enthalpy Heat 1  0.2° C. 0.26 J/g * ° C. None None 213.7° C.44.7 J/g Heat 2 17.0° C. 0.59 J/g * ° C. 113.7° C. −34.2 J/g 211.4° C.41.2 J/g Heat 3 17.0° C. 0.51 J/g * ° C. 121.4° C. −35.3 J/g 204.2° C.38.5 J/g

To prepare the copolymeric resin for processing into a precursor webmaterial, approximately 100 grams of the copolymer was heated overnightunder vacuum (<40 mm Hg) between 115° C. and 135° C. The resin waspelletized by grinding the copolymer through a granulator equipped witha screen having four (4) mm holes (Model 611-SR, Rapid Granulator,Rockford, Ill., USA).

A one-half inch screw extruder (Model RCP-0500, Randcastle ExtrusionSystems, Inc., Cedar Grove, N.J., USA) with an attached fiber spin packassembly (J. J. Jenkins, Inc., Matthews, N.C., USA) was obtained. Thebottom portion of the spin pack assembly had a seven (7) orificespinnerette (see “Spin Pack” in FIG. 5) consisting of 0.33 mm (0.013inches) diameter die openings arranged in a 2.06 cm (0.812 inches)diameter circular configuration. The spin pack was set to a temperatureof between 250° C. and 270° C. The particular temperature was dependenton inherent viscosity characteristics of the resin.

An adjustable arm holding a Vortec Model 902 TRANSVECTOR® (VortecCorporation—Cincinnati, Ohio USA) was attached to the spin pack andpositioned in alignment with the travel direction of a screen fabriccollector belt and below the base of the spinnerette (FIG. 5). The topof the TRANSVECTOR® inlet was centered below the die openings at anadjusted distance “A” (FIG. 5) of approximately 2.5 to 3.8 cm (1.0 to1.5 inches). The arm was mounted on a mechanical apparatus that causedthe TRANSVECTOR® to oscillate across the fabric collector in the samedirection as a moving take-up belt. The arm oscillated between anglesapproximately five (5) degrees off center at a frequency of rate ofapproximately 0.58 full sweep cycles per 2° second (approximately 35full cycles per minute). The TRANSVECTOR® was connected to a pressurizedair source of approximately 50 to 55 psi (0.34-0.38 MPa). Thepressurized air was at room temperature (20-25° C.), a temperature inexcess of the polymer's T_(odt). When operating, the pressurized air wasintroduced and accelerated within the TRANSVECTOR®'s throat. Theaccelerated air stream drew additional air into the inlet from the areaof the multiple orifice die.

The vacuum dried pelletized copolymer was then fed into the screwextruder (101) and through the crosshead of the spinneret (102) asillustrated in FIG. 5. The melted copolymer exited the spinnerette inthe form of seven (7) individual filaments (105). As the filamentsbecame influenced by the air current entering the TRANSVECTOR® inlet(103), the filaments were accelerated through the TRANSVECTOR® at asignificantly higher velocity than without the air entrainment.

The accelerated filaments were then accumulated on a screen fabriccollector belt (106) located at a distance “107” 66 cm (26 inches) fromthe outlet of the TRANSVECTOR® and moving at the speed of approximately20.4 cm/min (0.67 feet per minute) to form a precursor web material(108). Increasing the belt speed produced a thinner web material, whileslowing the belt speed produced a thicker web material.

The resulting unannealed, unstretched, non-woven, filamentous,self-cohered precursor web material that accumulated on the collectorbelt possessed a relatively consistent loft along the direction of beltmovement and possessed approximately 3.2 inches of “usable width.”“Usable width” refers to an inner portion of the precursor web materialhaving the greatest consistency at a gross, visual level, and a fine,microscopic, level. Portions of precursor web material outside the“usable width” have filaments that accumulate in such a way that theoverall web diminishes in relative height and density on either side ofthe centerline when observed in line with the direction of beltmovement. Area densities reported herein were obtained fromrepresentative samples acquired from a region of the web having a“usable width.”

After more than 10 seconds of cooling at ambient temperature, theprecursor web was removed from the fabric belt. Upon examination, thematerial was a tactilely supple, cohesive fibrous web, with individualcomponent fibers that did not appear to fray or separate from the webwhen subjected to moderate handling. The filaments were intermingled andbonded at contact points to form an un-annealed (i.e. minimallycrystallized or “unset”), unstretched, non-woven, self-cohered precursorweb material.

Precursor webs produced in this manner typically possess inherentviscosity (IV) values and crystallization exotherm peaks similar tothose described in Example 2 of U.S. Pat. No. 6,165,217, issued toHayes, and incorporated herein by reference. Particularly pertinentportions of the example are reproduced herein as follows.

Inherent Viscosity

Approximately 29 mg of the above-described precursor web was dissolvedin 25 ml of hexafluoroisopropanol (HFIP) to produce a dilute solution.The solution possessed an inherent viscosity (IV) of 0.97 dl/g whenmeasured using a Canon-Ubbelohde viscometer immersed in a 30° C.(+/−0.05° C.) water bath. Consequently, the IV was observed to havedropped during processing from the initial value of 1.53 dl/g in thepelletized copolymer to a value of 0.97 dl/g in the precursor web.

Thermal Properties

An appropriately sized sample was obtained from the above-describedprecursor web to allow for its thermal analysis utilizing a Perkin ElmerDSC7 Differential Scanning Calorimeter (DSC). Scanning was conducted at10° C./minute and the instrument's temperature was moderated with anIntracooler II refrigeration unit. A single scan between minus twentydegrees centigrade (−20° C.) and 250° C. was performed with thefollowing results (TABLE 2).

TABLE 2 T_(g)/T_(odt) Exotherm Exotherm Melt T_(g)/T_(odt) Capacity PeakEnthalpy Melt Peak Enthalpy Heat 1 16.32° C. 0.54 J/g * ° C. 88.16° C.−31.68 J/g 209.70° C. 45.49 J/g

The order-disorder transition temperature (T_(odt)) reported hereinoccurs at the inflection point between the differing levels of heatcapacity as indicated by a deflection of greater than 0.1 joule pergram-degree Celsius (J/g*° C.) in the baseline of the scan. This T_(odt)occurs at a temperature between the glass transition temperatures(T_(g)) of the respective homopolymers and is roughly approximated bythe Fox equation. In this particular example, the precursor web sampledisplayed an order-disorder transition at approximately 16° C. and acrystallization exotherm beginning at approximately 70° C. Full specimencrystallinity is considered proportional to the area under the meltendotherm, quantified by enthalpy in Joules/gram (J/g). The generalcharacteristics of a thermal scan of this precursor web can be observedin FIG. 3 of the above-referenced '217 patent.

Assuring that the web was not exposed to combinations of heat or timethat would lead to a substantial reduction of the precursor web'scrystallization exotherm enthalpy, as measured through theaforementioned evaluation with a power compensation based DSC system,opposite ends of rectangular segments of the precursor web were thenplaced under restraint and stretched in a single, or uniaxial,transverse direction (i.e., in a direction approximately 90 degrees fromthe longer length of the precursor web).

The highly porous stretched self-cohered web materials of the presentinvention were made with a transverse expansion/stretching machineequipped with pin grips and three electric heating zones. Such a machineis also known as an adjustable tenter or stenter frame with thecapability to expand transversely across the surface of a supportingmetal sheet while moving in a longitudinal direction. Due to broadadjustability, various machines able to fulfill the functions describedherein are available from numerous suppliers, one of which is: Monforts,A Textilmaschinen GmbH & Co KG, Moechengladbach, Germany.

This particular unit was equipped with three (3) sequential conjunctheated platens measuring 24, 6, and 24 inches (61, 15.2, and 61 cm) inlength, respectively. The heated platens created heated zones throughwhich the web material was passed. The leading edge of a 13 inch (33 cm)long stretching-transition region began 11 inches (27.9 cm) from theleading edge of the first heated zone. The initial feed rate was one (1)foot (30.48 cm) per minute.

In the initial stretching operation, only the third, or last downstream,zone of the stretching machine was heated to a temperature of 120° C.However, it was serendipitously discovered that heat from the third zoneprogressively invaded the adjoining second and first zones in such a waythat the precursor web was warmed before it was stretched. Inter alia,this resulted in progressively improving uniformity of the final highlyporous web material. Precursor web materials were stretched at ratios of2:1, 3:1, 4:1, 5:1 and 6:1. Preferred materials were formed when zoneone (1) of the transverse stretching apparatus was set at a temperatureof 50° C. and the precursor web material stretched at a ratio of 6:1.

After thermosetting the stretched web at a temperature of about 120° C.for about one (1) minute, a highly porous self-cohered web material ofthe present invention was formed and allowed to cool to roomtemperature. Each piece of inventive material was found to be moreporous, supple, lofty, compliant, and uniform in appearance than asimilar non-woven self-cohering web made without pre-heating andstretching of the similar web in an un-annealed state.

Additional rectangular sections of precursor web materials werestretched at ratios of 8:1 and 10:1 using preheated platens set toapproximately 50° C., 75° C., and 125° C. for each successive heatedzone in the stretching apparatus. The first two heat zone settingsprovided a reliable “pre-warming” of the precursor web material. Thetemperatures, in excess of the T_(odt) reported in the '217 patent, weresufficient to facilitate mobility of the co-polymeric molecules of theprecursor web material and provide a more consistent final product. Thethird heated zone was set to a temperature that at least approximatedand likely exceeded the temperature of the crystallization Exotherm Peak(T_(cr)) described within the '217 patent, to anneal, or heat-set, thefinal web material.

Example 2

In this example, precursor webs produced using the various belt speedsand transverse expansion ratios described in Example 1 were obtained fora variety of web densities and stretch, or draw, ratios. Followingprocessing, scanning electron micrographs (SEM) were generated ofrepresentative areas of this embodiment of the present invention. Somecharacteristics of the stretched web of the present invention and thefilaments comprising the web were quantified as follows.

The cross-sectional diameter of the stretched filaments in each webmaterial of the present invention was determined by visually examiningthe SEMs. In each SEM, fifty (50) stretched filaments were randomlychosen and the diameter of a cross-section of each filament wasmeasured. The cumulative results of these filament cross-sectionaldiameters is contained in Table 3 and summarized in FIGS. 6 and 7. Thestretch ratios are expressed as multiples of “X.” For example, “0×”refers to unstretched precursor web material. “4×” refers to a 4:1stretch ratio. Tabulated features of the web were the mean, median,maximum, and minimum fiber diameter. In addition, both the number andpercent of the fifty (50) fibers found to be less than twenty (20)microns in cross-sectional diameter were tabulated.

TABLE 3 Fiber Dimensional Characteristics at Varying Stretch Ratios 0X4X 5X 6X 8X 10X Mean 31.3 19.3 19.2 20.2 19.0 16.0 Median 30.3 18.6 17.618.4 18.6 15.0 Web Sample 6 2 2 10 2 2 Count Fiber Count 2.8 32.0 34.030.5 35.0 40.5 (<20 um) % < 20 um 5.7% 64.0% 68.0% 61.0% 70.0% 81.0% % >20 um 94.3% 36.0% 32.0% 39.0% 30.0% 19.0% % > 50 um 1.3% 0.0% 0.0% 0.6%0.0% 0.0% Minimum (um) 17.0 7.6 9.6 10.6 9.7 7.3 Maximum (um) 59.4 37.338.9 41.9 38.2 39.1

When evaluated with this method, all the fiber cross-sectional diametersin the unannealed, unstretched, precursor web (0X) were observed to bebetween seventeen (17) and fifty-nine (59) microns. Further, over ninetypercent (90%) of the fibers had cross-sectional diameters within thetwenty (20) and fifty (50) micron range described in theabove-referenced '217 patent. The effect of stretching on the fiberdiameter is readily seen from this data. Filaments of unstretchedprecursor webs can be reduced in diameter when subjected to thestretching process of the present invention. The reduction in fiberdiameter is readily seen by contrasting the number of fibers in anunstretched web having diameters below twenty (20) microns (e.g., 5.7%)with the number of fibers of stretched webs having diameters belowtwenty (20) microns. The number of fibers with diameters less thantwenty (20) microns in a stretched material of the present inventionrange from an average of sixty four percent (64%) to eighty one percent(81%). Accordingly, substantial stretching of a precursor web causes asignificant reduction in fiber diameter in a substantial number of thefibers in the final stretched web material of the present invention.

Since these webs were stretched, or drawn, in a single direction, or“uniaxial” manner, it is notable from this same data that twenty (20) toforty (40) percent of the fibers in the stretched web have diameterslarger than 20 microns. This mix of fiber diameters within the stretchedweb resulted in an increase in the web material's overall loft. TheIncreased the loft of the stretched web material correlates with areduction in both the web's area density and the volume density. Volumedensity is directly related to porosity. Web materials of the presentinvention have increased porosity compared to similar unstretched webmaterials. Increasing porosity and correspondingly reducing volumedensity maximizes interstitial space within the web structure. Thesefeatures increase the opportunity for infiltration of host cells intothe web material. The number and type of cell inhabiting a web materialof the present invention have a direct effect on the bioabsorption ofthe web material.

To quantify the actual molecular orientation imparted by the stretchingprocess of the present invention, birefringence values were determinedfor a variety of filaments from webs of the present invention made withdifferent stretch ratios. Birefringence values were obtained byutilizing a sliding quartz wedge capable polarizing microscopepossessing both an optical grid and a circular rotating stage (e.g.Nikon Optiphot2-POL). Both filament cross-sectional diameter andbirefringence values were determined from a sampling of filaments thatwere either actively or passively isolated from the optical influencesof the surrounding web.

Assuring no physical distortion artifacts occurred during filamentisolation, cross-sectional diameter values were determined usingconvention light microscopy and birefringence values. The values wereacquired through utilization of a Michel-Levy chart. Such opticalequipment is available from various suppliers (e.g., Nikon America,Melville, N.Y.). Michel-Levy charts are also available from varioussuppliers (e.g., The McCrone Institute (Chicago, Ill.).

The birefringence values thus obtained were analyzed for a correlationwith filament diameter. It was found the relationship appeared to followa power function that could be approximated by the equation:Y=0.4726X^(−0.9979)with an R2 value of 0.8211 (see FIG. 8). Using this relationship andreferring to FIG. 8, it was determined that a filament with a twenty(20) micron cross-sectional diameter could be expected to possess abirefringence value of approximately 0.024. Thus, filaments havingcross-sectional diameters less than twenty (20) microns could bereasonably expected to possess birefringence values in excess of 0.025.

Example 3

As a result of stretching the material described in Example 1, both theamount of polymeric material per unit area (area density) and amount ofpolymeric material per unit volume (volume density) were reduced. Aprecursor web (produced at a belt speed of 0.67 feet/minute (20.4cm/minute)) was further processed in an oven set at 100° C. for 25minutes to completely anneal, or “heat-set,” the web material.

The unannealed, unstretched, self-cohered precursor web material wassubstantially similar to the web material disclosed in the '217 patent.A heat-set version of the precursor web material was determined to havean area density of approximate 23 mg/cm² and a volume density ofapproximately 0.16 g/cc. Commercially forms of this type of web areavailable from W.L. Gore & Associates, Inc., Flagstaff, Ariz., under thetradenames GORE Bioabsorbable SeamGuard and GORE Resolut Adapt LT. Eachof these unstretched web materials has an area density of 9.7 mg/cm² and8.4 mg/cm², respectively. Each web material also had a volume density of0.57 g/cc and 0.74 g/cc, respectively. This corresponded to a percentporosity of fifty-six (56) and forty-three (43), respectively.

After uniaxial stretching of a precursor web material of Example 1 at aratio of 6:1, the material was determined to have an area density ofapproximately 5.3 mg/cm². This represents a change in area density ofapproximately seventy-five percent (75%). The unstretched precursor webmaterial of Example 1 had a volume density of 0.16 g/cc. In contrast,the stretched web material of Example 1 had a volume density of 0.083g/cc. This represents a reduction in volume density of approximatelyfifty (50) percent.

The specific gravity of full density, unstretched, 67% PGA:33% TMC (w/w)polymer (ρ_(polymer)) has been reported to be 1.30 grams/cc (Mukherjee,D, et al; Evaluation Of A Bioabsorbable PGA: TMC Scaffold For Growth OfChondrocytes, Abstract #12, Proceedings of the Society for Biomaterials,May 2005). By comparing this reported polymeric density value with thevolume density of a web material of the present invention(ρ_(scaffold)), overall percentage porosity in the absence of additionalcomponents can be determined through the relationship:(ρ_(polymer)−ρ_(scaffold))÷ρ_(polymer)×100

As used herein, the term “percent porosity” or simply “porosity” isdefined as the void space provided within the external boundaries of thestretched self-cohering web, absent the inclusion of any fillers orother added components that may effectively reduce the availableporosity.

This evaluation showed that stretching the precursor web material ofExample 1 increased the percent porosity of the PGA:TMC precursor webmaterial from eighty-eight percent (88%) in the absence of additionalcomponents to approximately ninety-four percent (94%) in the absence ofadditional components. The resulting percent porosity in the absence ofadditional components of both the precursor and aforementioned 6:1stretched web is provided in Table 4. Table 4 also provides a summary ofthe area density, the volume density, and the percent porosity of theweb material before and after stretching.

TABLE 4 Physical Property Comparison of 6:1 Stretched Web Precursor 6:1Web @ 0.67 Stretched Percent (%) Observation feet/minute Web ChangeDensity PGA:TMC = 1.30 g/cc Area Density 23 5.3 −77% (in mg/cm²) VolumeDensity 0.158 0.083 −47% (in g/cm³) Percent Porosity in 88% 94%  7% theabsence of additional components

Example 4

This example describes generation of tensile stress-strain data foruniaxially stretched (6:1 stretch ratio) web materials of the presentinvention. The web materials were produced according to Example 1 withthe exception that the belt speed was 0.26 feet/minute (7.9 cm/sec).

Samples of stretched web materials of the present invention were cutinto shapes having a central strip and enlarged ends, much like that ofa “dog bone.” The dog bone-shaped specimens were approximately half thesize of those described for ASTM D638 Type IV (i.e., with a narrowdistance length of 18 mm and a narrow width of 3 mm). Testing wasconducted using an INSTRON® Tensile Tester Model No. 5564 equipped withan extensometer and 500 Newton load cell. The software package used tooperate the tester was Merlin, Version 4.42 (Instron Corporation,Norwood, Mass.). The gauge length was 15.0 mm. The cross-head rate (XHR)was 250 mm/minute. Data was acquired every 0.1 second.

The percentage (%) elongation and matrix tensile stress of the stretchedweb, as measured from test specimens oriented in their length to be inline with in the stronger cross-web direction, was found to be 32.0% and60 MPa, respectively. The percentage (%) elongation and matrix tensilestress of the stretched web, as measured from test specimens oriented intheir length as measured in the weaker down-web direction, was found tobe 84.7% and 3.4 MPa, respectively. Tensile stress results for these67:33-PGA:TMC webs are summarized in Table 5 For comparative purposes,the mechanical characterization of a thinner web of 67:33-PGA:TMC asdescribed in the '217 patent is included in Table 5.

Matrix tensile stress is utilized as a means to normalize tensile stressin samples where measurement of thickness can be problematic, such asmaterials of the present invention possessing a high degree of porosityand easily deformed loft. Through utilization of the test material'sarea density and the specific gravity of its component polymer, thematrix tensile stress approach converts a difficult to measure porousloft into an equivalent thickness of full density component polymer. Thereduction is proportional to the volume density of the web divided bythe specific gravity of the component polymer. This equivalent polymericthickness was then utilized for cross-sectional area determinations inthe calculation of tensile stress. Such use of matrix tensile stress hasbeen described in both U.S. Pat. No. 3,953,566, issued to Gore, and U.S.Pat. No. 4,482,516, issued to Bowman, et al. for utilization indetermining the strength of porous expanded polytetrafluoroethylene(ePTFE) materials.

To obtain matrix tensile strength, the equivalent thickness of a tensilespecimen is determined by dividing the porous structure's area densityby the specific gravity of the component polymer. This value is thensubstituted instead of the specimen's actual thickness in determiningstress. Thus:Equivalent thickness=area density/specific gravity of polymer

Provided both the area density and the specific gravity of the componentpolymer are known, this equivalent thickness value can also be utilizedto convert the tensile stress of a porous sample into a matrix tensilestress value. In Example 2 of the '217 patent, both maximum tensilestress of the 67:33-PGA:TMC web material was reported along with thearea density of the test specimen and were found to be 4.9 MPa and 28.1mg/mm², respectively.

Thus, matrix tensile stress can be calculated as follows:

${\frac{4.9\mspace{14mu} N}{{mm}^{2}} \times \frac{{mm}^{2}}{\lbrack {{( {28.1\mspace{14mu}{mg}\text{/}100\mspace{14mu}{mm}^{2}} )/1.3}\mspace{14mu}{mg}\text{/}{mm}^{3}} \rbrack \times 1\mspace{14mu}{mm}}} = {22.7\mspace{14mu}{MPa}}$

TABLE 5 Tensile Max Matrix Density Max Force Stress Stress % Area VolumeSample Description (N) (MPa) (MPa) Elongation (mg/cm²) (g/cm³)Unstretched Precursor n.a. n.a. n.a. n.a. 44 .17 Web U.S. Pat. No.6,165,217 Not 4.9 22.7 Not 28.1 0.29 (Example 2; provided (saline)(calc'd) provided orientation not specified) 6:1 Transverse Stretched14.3 3.6 60 32.0 9.6 .065 Cross-Web Sample 6:1 Transverse Stretched 1.00.34 3.4 84.7 11.5 .078 Down-Web Sample n.a. = not acquired

As can be seen for the data, the web material of the present inventionwas found to be highly anisotropic and possessed reduced strength andsignificant elongation in the “down web” direction. Conversely, thestrength was highest in the direction of stretching and cross-web matrixtensile stress was found to be significantly higher than the fullycrystallized unstretched web material described in the '217 patent. Thisresult provided evidence of increased molecular orientation of thePGA:TMC block copolymers.

Example 5

This example describes the formation of an article of the presentinvention using an ABA triblock copolymer of PGA:TMC having a ratio ofpoly(glycolide) to poly(trimethylenecarbonate) (w/w) of 50:50.

Synthesis of a typical 50% PGA:50% TMC resin lot has been previouslydescribed in the '217 patent and is reiterated herein as follows.

A 4CV Helicone Mixer (Design Integrated Technologies, Warrenton, Va.,USA) located within a Class 10,000 clean room and connected to aSterling brand hot oil system (Model #S9016, Sterling, Inc., Milwaukee,Wis., USA) able to maintain temperatures up to 230° C. was pre-cleanedto remove any polymeric or other residues and then thoroughly air driedfor 2 hours before reattachment of the mixer bowl. The dry mixer wasthen preheated to 140° C. followed by a purge and then blanketing withanhydrous nitrogen a minimum flow during the course of the experiment. Afoil package containing 740.7 grams of trimethylene carbonate was openedand the contents introduced followed by mixing at a speed setting of“6.5.” After 10 minutes, stirring was stopped and 2.73 grams of acombination of 0.228 grams of SnCl₂.2H₂O catalyst and 15.71 grams ofdiethylene glycol initiator was then added directly to the melted TMC.Mixing was recommended and after 10 minutes the temperature was raisedto 160° C. which was then followed by an increase to 180° C. after 30minutes. After an additional 30 minutes, 75 grams of glycolide monomerwas added followed by an increase of the temperature to 200° C. After 15minutes, 675 grams of glycolide were added and the temperature settingimmediately changed to 220° C. After 40 minutes, the polymerized productwas discharged at the 220° C. onto a clean release surface where itsolidified as it cooled down to room temperature. The light brownpolymer thus obtained was then packaged in a pyrogen free plastic bagand then mechanically granulated through a 4.0 mm screen prior tofurther analysis and processing.

In the '217 patent, Hayes additionally reported the inherent viscosity(IV) of this particular 50% PGA:50% TMC resin lot to be 0.99 dl/g.

A 50% PGA:50% TMC triblock co-polymer synthesized as described was thengranulated as described in Example 1 and subsequently vacuum dried forat least 15 hours at 120° C. to 130° C. Approximately 250 grams ofground polymer was placed into the extruder described in Example 1 andheated to a die temperature of approximately 230° C. to 250° C. A randomcontinuous precursor web material, approximately 3.2 inches (5.08 cm) inwidth, was acquired at a belt speed of approximately 20.4 cm/min (0.67feet per minute). The precursor web material was morphologically similarto the unstretched 67:33-PGA:TMC precursor web material described inExample 1. The individual filaments formed cohesive bonds at contactpoints to form a self-cohered web. The filament diameter for webmaterials produced through this process ranged from twenty-five (25)microns to forty (40) microns. As noted in the '217 patent, these webmaterials typically have inherent viscosity values of 0.9 dl/g. TypicalDSC values for these web materials are listed in Table 6.

TABLE 6 Typical DSC Values for Unset PGA:TMC (50:50) Precursor WebT_(g)/T_(odt) Melt Ca- Exotherm Exotherm Melt En- T_(g)/T_(odt) pacityPeak Enthalpy Peak thalpy Heat 1 5° C. 0.5 110° C. −33 J/g 203° C. 37J/g J/g * ° C.

Stretching of the unannealed, non-woven, self-cohered, precursor webmaterial was conducted with the same equipment and uniaxial stretch rateas described in Example 1 for the 67:33-PGA:TMC triblock co-polymericnon-woven, self-cohered precursor web material. Care was taken that theunstretched precursor web was not exposed to combinations of heat ortime that would lead to a substantial reduction of the web'scrystallization exotherm enthalpy prior to stretching.

In addition to the uniaxial stretch ratios described in Example 1,additional uniaxial stretch ratios from 7:1 through 10:1 were performed.The oven temperature for zone one (1) was set at forty degreescentigrade (40° C.) and zone three (3) was set at eighty-five degreecentigrade (85° C.). Thermal setting of the stretched web wasaccomplished after approximately one (1) minute in zone three (3) ateighty-five degrees centigrade (85° C.).

For webs of the present invention made with a 50:50 PGA:TMC triblockcopolymer starting material, uniaxial stretch ratios of 7:1 through 10:1produced webs with the most suppleness and uniform appearance.

Example 6

This example describes the formation of an article of the presentinvention using multiple layers of precursor web material and stretchingthe layered material sequentially in perpendicular directions.

A starting material was obtained by layering together nine sheets ofunannealed, unstretched, precursor web material made according toExample 1. Each of the nine precursor sheets was produced at a beltspeed of 1.58 ft/minute (48 cm/min). Each precursor sheet was found tohave an area density of approximately 9.0 mg/cm² and a volume density ofapproximately 0.27 g/cc. Accordingly, nine layers of precursor sheetmaterial would be expected to have an area density of approximately 81mg/cm² and a volume density of approximately 0.27 g/cc.

The nine unannealed, unstretched, precursor web sheets were initiallyoriented so their width was generally in the same “machine direction” asthe moving belt used to take up the web as it was formed. The similarlyoriented layered sheets were stretched transversely (i.e., in adirection approximately 90 degrees from the direction of initialorientation of the unannealed web) in an oven with each of three heatedzones set at ambient temperature, 50° C., and 120° C., respectively. Thestretch ratio was 6:1 and the stretch rate was one foot per minute (30.5cm/min).

The result was an article of the present invention having an areadensity of 18 mg/cm². This represents nearly a seventy-six (76) percentreduction in area density from the precursor web material. The articlehad a volume density of 0.11 g/cc. This represents nearly a sixty (60)percent reduction in volume density from the precursor web material(0.27 g/cc). The percent porosity of this web material was seventy-nine(79).

The percentage of elongation of the precursor web and the matrix tensilestress of the finished laminated web material was measured in thestronger cross-web direction and found to be sixty-four percent (64%)and 48 MPa, respectively. The percent elongation and matrix tensilestress of the finished laminated web material of the present invention,as measured in the weaker down-web direction, was found to be onehundred thirty-three percent (133%) and 5.2 MPa, respectively. Thesesvalues are greater than those observed with the single layer uniaxiallydistended web of Example 1. Matrix tensile stress in the cross-webdirection were also higher than the 22.7 MPa values reported in the '217patent.

The layered web material of this example possessed increased supplenessand uniform appearance compared to a non-stretched, non-woven,self-cohered layered web material.

Example 7

This example describes materials produced from a first longitudinal webstretching procedure, followed by a subsequent transverse stretchingprocedure of the same web. This web material is referred to herein as a“Longitudinal-Transverse Stretched Web.” Unannealed, unstretched,self-cohered precursor web material was prepared in accordance withExample 1 and processed as follows to form a material of the presentinvention. The precursor web material had an area density ofapproximately 45 mg/cm².

When evaluated using DSC parameters as described in Example 1, thethermal characteristics of both the utilized 67:33-PGA:TMC resin and theresulting unannealed precursor web were those summarized in Table 7.

TABLE 7 DSC Values for Unset 67:33 PGA:TMC Precursor Web T_(g)/T_(odt)Exotherm Exotherm 1 scan T_(g)/T_(odt) Capacity Peak Enthalpy Melt PeakMelt Enthalpy Resin 13.5° C. 0.33 J/g * ° C. none none 193° C. 40.5 J/gWeb 18.4° C. 0.57 J/g * ° C. 82.9° C. −30.1 J/g 196° C. 39.5 J/g

Five (5) varieties of stretched web material of the present inventionwere produced in this example based primarily on stretch ratio. Using alongitudinal stretching machine able to draw precursor web of suitablelength across the surface of a supporting three zone heated metal sheetwhile moving in a longitudinal direction between dissimilar speedadjusted feed and take-up rollers, each unannealed, unstretched,precursor web material was first longitudinally stretched at a ratio of1.5:1 at a temperature of twenty degrees centigrade (20° C.) in adirection substantially the same as the direction of the collector beltused for retrieval of the unstretched precursor web. This longitudinaldirection (e.g., x-axis direction) is referred to herein as the“down-web” (DW) direction.

The longitudinally stretched unannealed, self-cohered, web material wasthen transferred to the heated platen transverse stretching machinedescribed in Example 1. Each of these down-web stretched materials wassubsequently stretched a second time in a “cross direction” (y-axis)perpendicular to the direction of the first longitudinal stretchingprocedure. This “cross-direction” stretching is referred to herein as“cross-web” (CW) stretching. The first sample (designated “1B”) wasstretched cross-web at a ratio of 2:1. The next sample (“2A”) wasstretched cross-web at a ratio of 3:1. Each remaining sample (2B, 2C,and 2D) was stretched cross-web at a ratio of 3.5:1, 4:1, and 4.5:1,respectively. The first and third heated zones in the oven were set tofifty degrees centigrade (50° C.) and one hundred twenty degreescentigrade (120° C.), respectively. The temperature in zone three wassufficient to completely heat-set the final stretched web material ofthe present invention. The resulting material was a fully annealed web,as is evidenced by the thermal characteristics displayed in Table 8 thatdisplayed substantial DW extendibility.

TABLE 8 DSC Values for Longitudinal-Transverse 67% PGA:33% TMC WebT_(g)/T_(odt) Exotherm Exotherm 1 scan T_(g)/T_(odt) Capacity PeakEnthalpy Melt Peak Melt Enthalpy 1B 11.8° C. 0.39 J/g * ° C. none none193° C. 38.6 J/g 2A 11.4° C. 0.35 J/g * ° C. none none 192° C. 38.9 J/g2B 11.6° C. 0.33 J/g * ° C. none none 194° C. 41.0 J/g 2C 11.1° C. 0.30J/g * ° C. none none 192° C. 38.8 J/g 2D 11.3° C. 0.32 J/g * ° C. nonenone 192° C. 38.2 J/g

The physical and tensile stress-strain properties of the (1.5:1)longitudinal-(4.5:1) transverse stretched web (2D), along with a fullyset precursor web, are summarized in Table 9.

TABLE 9 Physical & Mechanical Properties of Longitudinal-Transverse67:33 PGA:TMC Web Tensile Max Max Matrix Density Force Stress StressArea Volume Sample Description (N) (MPa) (MPa) (mg/cm²) (g/cm³)Unstretched Precursor 9.0 3.6 16.9 22.5 0.28 Web Down Web Sample 2D -1.3 2.3 10.3 5.2 DW (3:2 DW by 5:1 CW) Cross Web Sample 2D - 4.8 5.023.1 8.4 CW (3:2 DW by 5:1 CW)

Example 8

This example describes formation of two stretched self-cohered webmaterials of the present invention. The web materials weresimultaneously stretched bi-axially in two directions (x-axis andy-axis) during processing.

An unstretched precursor web material was made according to Example 1.The TRANSVECTOR® apparatus was set at a spinneret angle of 8.5 degreesand a sweep rate of approximately 0.46 full cycles per second. Theresulting unannealed, unstretched, precursor web material had a “usablewidth” of five (5) to six (6) inches (12.7 cm to 15.2 cm) with a webdensity of forty (40) to fifty (50) mg/cm² produced at a belt speed ofapproximately 8 cm/min. The unannealed, unstretched, precursor webmaterial was not exposed to interim combinations of heat or time thatwould lead to a substantial reduction of the web's crystallizationexotherm enthalpy.

A pantograph was used to biaxially stretch the unannealed precursor webmaterial to form a first bi-axially stretched web material. A pantographis a machine capable of stretching the precursor web material biaxiallyor uniaxially over a range of rates and temperatures (e.g., 50° C. to300° C.). The pantograph used in this example was capable of stretchinga piece of precursor web material from a four inch by four inch (4″×4″)square piece to piece twenty-five inches by twenty-five inches(25″×25″). This represented a 6.1:1 stretch ratio in both x and y axes.To retain the precursor web material while stretching, the lasthalf-inch of each arm on the pantograph was equipped with a pin array.There were a total of thirty-two (32) arms on the pantograph—seven oneach side, plus one in each corner. The pantograph was also equippedwith heated clamshell platens, which permitted control of thetemperature of the precursor web material during processing.

The first bi-axially stretched web material was made by fixing a five(5) inch (12.7 cm) square piece of unannealed, unstretched, precursorweb material (45 mg/cm²) onto the pantograph pin-frame at an initialsetting of four inches by four inches (4″×4″). The clamshell platenswere set at fifty degrees centigrade (50° C.) and were positioned overthe unannealed web for two minutes to pre-heat the precursor webmaterial in excess of the polymer's T_(odt) prior to stretching. Thepre-heated precursor web material was stretched sequentially at a ratioof 3.6:1 along the x-axis (down-web) and a ratio of 6.0:1 along they-axis (transverse), both at a rate of 20 percent per second (20%/sec).Upon completion of the stretching process, the platens were retractedfrom the bi-axially stretched web material.

A pin frame, twelve (12) inches long by eight (8) inches wide, wasinserted into the bi-axially stretched web material of the presentinvention to restrain a portion of it after it was removed from thepantograph pins. The bi-axially stretched web material was thenheat-set, while restrained in the eight (8) inch by twelve (12) inchpin-frame, in an oven set at one hundred twenty degrees centigrade (120°C.) for about three (3) minutes. The resulting first biaxially stretchedweb material was removed from the pin-frame and the unrestrained portiontrimmed away.

The first biaxially stretched web material was tested for area weightand thickness. From these measurements the volume density and porositywas calculated, as taught in Example 3. The area weight was measured asdescribed in Example 1. The thickness was measured per the procedure inExample 1, except that a glass slide, 25 mm×25 mm×1 mm thick, was placedon the top of the web in order to clearly distinguish the upper surfaceof the web on the optical comparator. The area weight was 2.61 mg/cm²,which represents about a ninety-four percent (94%) reduction of theunannealed precursor web material area weight. The thickness was 0.44mm. These values give a volume density of 0.059 g/cm³ and a percentporosity of ninety-five (95). This percent porosity value is two-foldgreater in void to solids ratio (void volume/solids volume) than thehighest porosity disclosed in the '217 patent.

A second bi-axially stretched web material was made as described aboveexcept for modifications in several process parameter settings. For thissecond stretched web material, the preheat temperature was set to 70° C.and the unannealed web was pre-heated for about 30 seconds. The web wassimultaneously stretched at a ratio of 3.6:1 along the x-axis and aratio of 6.0:1 along the y-axis at the same stretch rate of thirtypercent per second (30%/sec). The second bi-axially stretched webmaterial was restrained and heatset on a pin-frame in an oven asdescribed above for the first stretched web material.

The properties of the second bi-axially stretched web material weremeasured as described for the first stretched web material. The areaweight was 3.37 mg/cm² and the thickness was 0.94 mm. This gave a volumedensity and porosity value of 0.036 g/cm³ and 97%, respectively. Thevoid to solids ratio of the second bi-axially stretched web material isabout 50% greater than the that of the first bi-axially stretched webmaterial and about 3-fold greater than that disclosed in the '217patent.

Example 9

This example describes formation of a stretched web material of thepresent invention. The stretched web material has increased loft andsuppleness and substantially resumes its original shape when an applieddeforming force is removed.

A biaxially-stretched web material was made according to Example 8except that a pin-frame was not used to restrain the web material as itwas heat-set in the oven. Rather, the bi-axially stretched web materialwas suspended loosely in the oven from a rack as it was set. Thebi-axially stretched web material was observed to contract after removalfrom the pantograph. The bi-axially stretched web material contractedfurther in the oven. The area of the fully stretched starting webmaterial was reduced by about fifty percent (50%) with this process.

The resulting highly porous, bi-axially stretched and contracted, webmaterial was thicker, softer, loftier, and more flexible than eithersimilarly-produced stretched web material of Example 8. In addition,this bi-axially stretched and contracted web material resumed itsoriginal shape when an applied deforming force was removed. Thisresilient property was found in all portions of the bi-axially stretchedand contracted web material. Microscopic examination (50×) of theresilient bi-axially stretched and contracted web material revealedhighly curved self-cohered filaments of the material oriented in alldirections, including the z-axis (i.e., perpendicular to the planar xand y axes). The diameter of these “z-axis oriented fibers” was similarto those of the “x-axis” and “y-axis” oriented fibers. The resultinghighly porous, resilient, bi-axially stretched and contracted,self-cohered, bioabsorbable, polymeric web material of the presentinvention possessed physical and handling characteristics similar tofabrics commonly referred to as “fleece.”

The properties of the bi-axially stretched and contracted fleece webmaterial were determined per the methods described in Example 9 and arecompared to the second biaxially stretched web of Example 8 in Table 10below:

TABLE 10 Property Example 9 Example 8 Area Weight (mg/cm²) 5.13 3.37Thickness (mm) 2.11 0.94 Volume Density (g/cm³) 0.024 0.036 Porosity(%)in the 98 97 absence of additional components Void/Solids Ratio 49 32

FIG. 4 is a scanning electron micrograph (SEM) showing filaments ofthese materials oriented in multiple directions following the stretchingprocess. Under ten-times (10×) magnification, a number of the filamentsappeared to be oriented in a direction perpendicular (z-axis) to theother filaments oriented along the x and y axes of the material. Onvisual inspection, the thicker articles of the present invention had afleece-like appearance having a deep pile, high degree of loft, and veryhigh percent porosity.

Example 10

This example describes the formation of articles of the presentinvention by stretching precursor web material radially in alldirections simultaneously. Both single and multiple layered precursorweb materials were radially stretched in this example. In someembodiments, these multiple layered precursor web materials becamelaminated together in the finished web material.

In each embodiment, at least one piece of a 67:33-PGA:TMC precursor webmaterial made according to Example 1 was cut into circular pieces havingan initial diameter of six (6) inches (15.24 cm). Embodiments utilizingmultiple layers of precursor web material were formed by placing severallayers of the precursor web material together prior to cutting. For eachembodiment, the circular material was restrained in a clamping apparatuscapable of stretching the precursor web material in all directions at anequal rate within a temperature controlled environment.

In each embodiment, eight clamps were placed equidistant around theperiphery of the particular precursor web material approximatelyone-half (0.5) inch in from the edge of the web material. Thiseffectively reduced the initial diameter of the precursor web materialfrom six (6) inches to five (5) inches (12.7 cm). The clamped precursorweb material was preheated at a temperature of 50° C. for approximatelytwo (2) minutes to raise the precursor web material above theorder-disorder temperature (T_(odt)) of the particular polymer systemused to make the precursor web material. The softened precursor webmaterial was then stretched at a rate of 0.25 inches/second until theweb had a diameter of twelve (12) inches (30.48 cm). The four-layeredmaterial was stretched to a final diameter of 14 inches (35.56 cm) atthe same stretch rate. While retained in the stretched configuration,the stretched web material was heated to 120° C. for two (2) to three(3) minutes to heat-set the stretched web material.

The parameters of layers, precursor web material area weights, andstretch ratios (final diameter/initial diameter) of each article arelisted in Table 11, below. The total area weight of the precursor webmaterial is the product of the precursor layer area weight and thenumber of layers. For example, the gross precursor area weight ofarticle 10⁻² was about 90 mg/cm² (2 layers×45 mg/cm²). Article 10⁻⁶ wasproduced to a uniform appearance, but was not quantitatively tested.Also listed in the table is the area weight of the finished stretchedweb.

TABLE 11 Area Weight Precursor Layer Area Stretch of Stretched ArticleID Layers Weight (mg/cm²) Ratio Web (mg/cm²) 10-1 1 45 2.8 3.68 10-2 245 2.4 9.43 10-3 2 22 2.8 5.87 10-4 2 10 2.8 2.75 10-5 4 10 2.8 5.4010-6 6 45 2.4 Not measured

FIG. 4A is a scanning electron micrograph (SEM) showing filaments of aradially stretched self-cohered web material of the present invention.The image, which depicts filaments oriented radially in multipledirections following the stretching process, is of an alternativeembodiment fabricated from 50% PGA:50% TMC copolymer.

Example 11

This example provides a compilation of porosity values observed invarious embodiments of the present invention. Initially, precursor webmaterials as described in Example 1 were prepared at belt speeds of 7.9,14.0, 20.4, and 48.0 cm/min, annealed under restraint, and thenevaluated for volume density and percent porosity. The percent porosityvalues were determined by controlling the height of the finished webmaterial with a glass microscope slide and an optical comparator asdescribed in Example 8. Stretched web materials of the present inventionhaving the highest percent porosity values were obtained with a beltspeed of 48.0 cm/min.

Appropriately sized samples of precursor web materials were eithertransversely stretched as described within Example 1 or bi-axiallystretched as described in either Example 8 or 9. The precursor webmaterial and several finished stretched web materials were thenevaluated for average percent porosity. The percent porosity results andaccompanying processing parameters are presented in Table 12. As seenfrom Table 11, the highest percent porosity possessed by the precursorweb material was 89.7%. Accordingly, all stretched, self-cohered, webmaterials of the present invention have percent porosity values of atleast ninety percent (90%).

TABLE 12 Porosity of Various Precursor and Stretched Web StructuresPercent porosity in Belt Stretch Ratio the absence Fabrication SpeedTransverse x- of additional Method BS (cm/min) or y-axis axis components(Example #) Precursor 48 n.a. n.a. 89.7 1 Biaxial 7.9 6:1 3.6:1 97.3 8Biaxial 20.4 6:1 3.6:1 96.8 8 Biaxial- 7.9 6:1 3.6:1 98.1 9 FleeceUniaxial 7.9 5:1 89.8 1 Uniaxial 7.9 6:1 90.7 1 Uniaxial 7.9 7:1 91.8 1Uniaxial 13 5:1 92.5 1 Uniaxial 13 6:1 92.7 1 Uniaxial 13 7:1 90.9 1Uniaxial 14 6:1 94.0 1 Uniaxial 20 4:1 90.7 1 Uniaxial 20 5:1 92.2 1Uniaxial 20 6:1 93.2 1 Uniaxial 20 8:1 94.4 1 Uniaxial 48 5:1 94.6 1

As seen in Table 12, the percent porosity increased for all embodimentsof the stretched web material of the present when compared to precursorweb materials made by the present inventors to have as high a percentporosity as possible with currently available technology.

Example 12

This example describes the formation of an article of the presentinvention in a tubular form (FIG. 13).

In this example, a tubular article able to stretch in a radial directionwas formed utilizing a mandrel combination equipped with means forlongitudinal extension of a wrapped tube formed from an unset precursorweb. The utilized combination is composed of a smaller rigid rod or tube(“mandrel”) that can be at least partially contained within the insidediameter of a circumferential means for affixing the ends of the wrappedtube. At least one end of the tube is then slid by manual or mechanicalmeans along the axis of the mandrel to effect the desired longitudinalexpansion ratio. Alternatively, once the tube is formed and attached tothe circumferential fixation, the mandrel can be removed and expansionaccomplished through tensile extension.

Articles were formed by wrapping an approximately five inch (12.7 cm)length of an unannealed precursor web material (˜9 mg/cm²) made asdescribed within Example 1 around both a three-eighths inch (0.953 cm)diameter metal mandrel and a portion of the circumferential fixationsufficient to allow later physical attachment. Wrapping was achieved byslightly overlapping the opposing edges to form a “cigarette wrap.” Thisstep was repeated with offset seams to produce a multi-layered (i.e.,2-10 layers (5 layers preferred)) tube of unannealed precursor webmaterial.

Attachment of the tube to the fixation means was accomplished byaffixing the overlying ends of the tube against the circumferentialridge with a copper wire. The combination was then placed in a preheatedoven set at a temperature of 50° C. for approximately two (2) minutes tosoften the unset polymeric material. The softened material was thenstretched longitudinally at a ratio of approximately 5:1. This was 2°followed by fixing the sliding mandrel in place heating the combinationto 100° C. for five (5) minutes to set (i.e., anneal or fullycrystallize) the final article.

This tubular form of the present invention displayed an ability tochange from an initial first diameter to a larger second diameter whenexposed to radial expansion forces. The tube formed in this example wasfound to be readily distensible from a first diameter to a seconddiameter approximately two times larger than the first diameter.

Example 13

This example describes the formation of an article of the presentinvention in a tubular form having an ability to increase in diameterfrom a first initial diameter to a second larger diameter, combined withan ability to change axial length (FIG. 17).

As in the prior example, this article was formed by cigarette wrappingmultiple layers of unannealed web around both a three-eighths inch(0.953 cm) diameter metal mandrel and circumferential fixation. Thewrapped combination was then placed in an oven preheated at a settemperature of 50° C. for approximately two (2) minutes to soften theunannealed polymeric material. The softened material was then stretchedlongitudinally at a ratio of 5:1, the sliding fixation immobilized, andthe combination heated for 1 minute in an oven set to 100° C. Thecombination was removed and opposite ends of the now stretched tubularform were urged toward each other to a length approximately half that ifthe original extension distance so as to compact the material along itslength in an “accordion-like” fashion. The combination containing this“corrugated” tubular material was then heated to 130° C. for five (5)minutes to impart a complete set to the final article. Upon completionand removal of the article from the fixation, the article was observedto retain the corrugated structure, evidencing partial crystallizationat the 100° C. treatment conditions.

In addition to having the ready ability to change diameter when exposedto radial expansion forces, the article described in this example wasalso able to change in length. In addition, this article was moreflexible and exhibited greater resistance to kinking when bent into acurved conformation than the article described in the previous Example,supra.

Example 14

This example describes the formation of an article of the presentinvention in a tubular form having at least one framework componentincorporated into the article (FIG. 16).

A two layered fully set first tubular form was constructed as describedin Example 12, trimmed to approximately four inches in length, and thenleft on the mandrel without overlapping onto the circumferentialfixation. A 0.020 inch (0.051 cm) diameter copper wire was then wound ina helical manner around the outer surface of the tubular form withapproximately 0.25 inch (0.635 cm) spacing between windings. A secondtubular form made of precursor web material approximately 5 inches (12.7cm) wide was then closely wrapped over both the wire-wound first tubularform and a portion of the circumferential fixation sufficient to allowits physical attachment. The combination was then wrapped with anoverlying sacrificial polytetrafluoroethylene (ePTFE) pipe-tape stylefilm. Longitudinal stretching of the tubular form was then undertaken aspreviously described at a 5:1 stretch ratio to effect tube extensionsimultaneous with a reduction of the tubes inner diameter. This processeffectively compressed the outer tube into intimate contact with theunderlying metallic coil and inner tube. This wrapped construct was thenheated to 100° C. for five (5) minutes to heatset the article. Thesacrificial PTFE film was removed from the finished article.

The article thus produced was a metallic coil encased within bothoverlying and underlying layers of a flexible stretched, non-woven,self-cohered PGA:TMC tube. This construction could serve as animplantable intravascular medical device, such as a stent or stentgraft.

Example 15

This example describes the formation of a stretched self-cohered webmaterial of the present invention in the form of a rope or flexible rod(FIG. 14).

In this example, a stretched rope or flexible rod self-coheredfilamentous form was formed by longitudinally pulling and axiallytwisting a length (2.54 cm wide×25.4 cm long) of unannealed,unstretched, precursor web material (9 mg/cm²) to a point of tactileresistance. The length of precursor material was extended approximately15.25 cm (6 inches) and twisted approximately ten (10) times. Thematerial was then stretched along its longitudinal axis at a stretchratio greater than 2:1. In this example the precursor web material wasboth twisted and stretched by manual means, but mechanical methods maybe also be used.

The article was then restrained in its twisted form and heated in anoven set to a temperature of 50° C. for 1 minute, removed, and thenpromptly stretched along its longitudinal axis to a distance twice thatof its original length. The article was then restrained in its stretchedform and then heated in an oven set to 100° C. for 5 minutes to heatset(i.e., anneal or fully crystallize) the final article.

The finished article appeared to be a highly flexible rod or rope thatvisually appeared to possess a continuous pore structure through itscross section.

Example 16

This example describes the formation of a web material of the presentinvention having a very low volume density and very high percentporosity (FIG. 19).

While a porous stretched web material from any of the above-describedexamples is suitable for use as a starting material for this very highpercent porosity material, a web material made according to Example 1 ata 6:1 stretch ratio and an area density of 40-50 mg/cm² was obtained andused as the starting web material in this example.

The starting web material was subjected to a carding procedure by layingthe web material flat onto a granite surface plate, restraining the webmaterial by hand, and repeatedly abrading the filaments of the webmaterial in a random fashion with a wire brush. As the filaments of theweb material were abraded, at least some of the filaments of the webwere engaged and separated by the wires of the brush. As the filamentswere separated, the percent porosity of the web material increased andthe volume density decreased. The visual appearance of the finishedcarded web material was similar to a “cotton ball.”

In another embodiment, at least one metallic band is attached to the webmaterial (FIGS. 19A and 19B). The metallic bands can serve asradio-opaque markers to aid in visualizing the web material during andafter implantation.

As described in Example 17, this material has been shown to bethrombogenic and provide hemostasis in a variety of circumstances. Forexample, the carded web material of the present invention can stop, orsignificantly reduce, bleeding at an incision site in a major bloodvessel, such as a femoral artery. Bleeding can also be stopped orsignificantly reduced in puncture wounds, lacerations, or othertraumatic injuries. The carded web material described in this examplecan also be used to fill an aneurysm or occlude a blood vessel or otheropening in the body of an implant recipient.

The highly porous web material described herein can be combined with adelivery system (FIG. 20), such as a catheter, to aid in placement ofthe web material at an indirectly accessible anatomical site.

This web material can also be used as a component of an implantablemedical device to assist in providing a liquid seal for the deviceagainst an anatomical structure or tissue.

Example 17

This example describes the use of a very highly porous web material ofthe present invention to stop bleeding in an artery of an implantrecipient.

Using a domestic porcine model that had previously been heparinized, aneight French (8 F) guiding catheter was used to selectively access thecranial branch of the left renal artery. An angiogram was performed forbaseline imaging and the guide wire removed. A 6 F guide cathetercontaining a combination of an approximately 7 mm diameter by 20 mm longpiece of web material made according to Example 16 was then introducedinto the vasculature of the implant recipient through the length of the8 F catheter. The web material of Example 16 contained a radio-opaquemarker band to assist in remotely visualizing the present inventionduring and after implantation (FIG. 20).

The marked web material of Example 16 was then deployed into the cranialbranch of the above-mentioned left renal artery from the 6 F catheter.Following implantation of the marked web material in the renal artery,partial occlusion of the blood vessel was observed, via angiogram,within thirty seconds. Full occlusion of the blood vessel was observedat three (3) minutes post deployment. Occlusion was interpreted to becaused by coagulation of blood in the vessel at the implantation site,despite the presence of the heparin.

A second procedure was performed on this implant recipient todemonstrate the ability of the web material of Example 16 to stop bloodflow at an arterial incision site. A femoral laceration was created witha partial transaction of the femoral artery. The artery was occludedproximally, so only retrograde flow was present. Despite this conditionbleeding at the incision site was profuse. Two cotton ball size piecesof the web material of Example 16 were then applied to the arteriotomyand held under digital pressure for approximately 30 seconds. Thoughthere was some initial seeping of blood through the ball, the bleedingwas completely stopped at two minutes.

Example 18

Swine and canine with normal activated clot times (ACT) used for otheracute vascular patency studies were used in this Example for a model ofan organ laceration injury. In order to induce organ laceration, a 13 mmdiameter puncture was made in the liver or spleen of the implantrecipient with a modified trephine. The puncture was allowed to bleedfreely for forty-five (45) seconds. Approximately 1 gram of the highlyporous web material described in Example 16 was applied by hand into thepuncture with compression for one (1) minute. Pressure was then releasedand the wound evaluated for bleeding. If bleeding did not cease,pressure was re-applied for another minute and the evaluation repeated.

As a comparison, a commercially available chitosan-based haemostaticmaterial (HEMCON; HemCon Inc., Portland, Oreg.) was examined in the sameorgan laceration model. Both the highly porous web material described inExample 16 and the HEMCON material successfully produced haemostasisafter 1 minute compression. The ease of handling and implantation of thepresent invention was considered superior to the HEMCON product.

Though the web material of Example 16 is in a “cotton ball-like” form,other forms of the highly porous web material can be used for hemostasisand other medical circumstances requiring thrombogenic results. Theseforms include, but are not limited to, rolls or wads of the webmaterial. The high compressibility of the present invention allows forefficient packaging of the invention.

Example 19

This example demonstrates the thrombogenic properties of the presentinvention through the use of a comparative in vitro blood clotting testproviding results expressed in terms of relative clot time (RCT).

To determine an in vitro whole blood clot time for samples of differentthrombogenic materials, approximately two (2) mg of each test samplematerial was obtained and individually placed in a polypropylenemicrocentrifuge tube. The sample materials used in this test were porousweb materials made according to Examples 1 and 16, and two commerciallyavailable hemostatic materials, HEMCON® chitosan bandage (HemCon Inc.,Portland, Oreg.) and HEMABLOCK® hemostatic agent microporouspolysaccharide beads (Abbott Laboratories, Abbott Park, Ill.).

FIG. 18 illustrates the steps followed for the Relative Clot Time test.In the test, fresh unheparinized arterial blood was collected fromdomestic swine and immediately mixed with sodium citrate to a finalcitrate concentration of 0.0105 M. One (1) ml of the fresh citratedblood was added to each sample tube. To facilitate the clotting cascade,100 μl of 0.1 M calcium chloride was added to each sample tube. Thetubes were immediately capped and inverted 3 times. At each 30 secondinterval, the tubes were inverted for 1 second and returned to theirupright positions. The time was recorded when blood ceased to flow in asample tube. Each test included a positive control (calcium+citratedblood only) and negative control (citrated blood only). For every test,clot time was normalized to the calcium control, with the smaller valueindicating a faster overall time to clot.

The web materials made according to both Example 1 and Example 16 eachreduced the Relative Clot Time (RCT) to a value of approximately 0.7when compared to the positive citrated calcium control value of 1.0.These materials also displayed superior results to the commerciallyavailable hemostatic products HEMCON, with an experimentally observedRCT of 1.0. With the HEMABLOCK®) hemostatic agent powder an RCT of 0.9was observed.

Example 20

This example describes the formation of an article of the presentinvention to include a second bioabsorbable polymeric material (FIG. 9).

In this Example, a finished 6:1 web material according to Example 1 wasobtained and imbibed with a film made of carboxymethylcellulose (CMC).The CMC utilized was of the high viscosity (1500-3000 cps at one percent(1%) at twenty-five degrees centigrade (25° C.)) variety available fromSigma-Aldrich (St. Louis, Mo., USA), Catalog #C-5013. A CMC film wasformed from a gel concentration of 8 g CMC/100 ml distilled water (8%w/v). The film had a thickness approximately equal to the thickness ofthe web material to be imbibed. The film was produced by rolling a beadof 8% CMC gel onto a flat metal plate and allowing the film toconsolidate. The CMC gel film was then placed in contact with asimilarly sized piece of web material from Example 1 and tactilelypressed together between two suitable release surfaces for approximatelyone (1) minute at room temperature. The CMC-imbibed web material wasthen dried under vacuum at 40° C., with an occasional purge with air.

This process was repeated with CMC gel film placed on both sides of theweb material in a “sandwich” relationship.

When wetted with saline, water, or blood, the material described in thisexample generated a concentrated gel that displayed significantadherence that made the web readily conformable to the topography ofmany physical features. Such adherence was recognized as carryingpotential to assist a surgeon, interventionalist, or other healthcareprofessional in temporarily maintaining the present invention at aparticular anatomical location, implantation site, or in approximationto a surgical instrument or other implantable device. The CMC coating ineither dry or gel form may affect the permeation rate of variousphysiological fluids into or out of the underlying web material.

Example 21

This example describes imbibing carboxymethylcellulose (CMC) intointerstitial spaces of a finished 7:1 web material according to Example5, supra. To make this construction, high viscosity sodiumcarboxymethylcellulose (“CMC”; Sigma Chemical Company, St. Louis, Mo.)was dissolved in deionized water at a four percent (4%) concentration(i.e., 4 g/100 ml) using an industrial blender. Entrapped air wasremoved by centrifugation. The CMC solution was imbibed into thefinished web material (3.8 cm×10.2 cm) using a roller to completely fillthe porosity of the web. The CMC-imbibed web was air dried at roomtemperature for sixteen hours (16 hrs) to produce a CMC-imbibed,self-cohered, stretched PGA:TMC web material.

When wetted with saline, water, or blood, the material described in thisexample generated a concentrated gel that displayed significantadherence that made the web material readily conformable to thetopography of many physical features. Such adherence was recognized ascarrying potential to assist a surgeon, interventionalist, or otherhealthcare professional in temporarily maintaining the present inventionat a particular anatomical location, implantation site, or inapproximation to a surgical instrument or other implantable device.

Example 22

This example describes imbibing carboxymethylcellulose (CMC) intointerstitial spaces of a finished web according to Example 16 anddissolving the imbibed CMC from the web into a phosphate buffer saline(PBS) solution. To make this construction, 4% CMC was imbibed into asample of highly porous web material made according to Example 16 usinga roller to completely fill the void spaces. The imbibed web was airdried at room temperature for sixteen hours (16 hrs) to produce aCMC-imbibed high porosity, self-cohered, PGA:TMC web material. TheCMC-imbibed web of Example 16 was then immersed in a PBS solution. Uponimmersion, the CMC swelled to produce a hydrogel-filled, high porosity,self-cohered PGA:TMC web material. Upon immersion for an additional ten(10) minutes, the CMC appeared to dissolve into the PBS and elute fromthe web material.

Example 23

This example describes imbibing a carboxymethylcellulose (CMC) intointerstitial spaces of a web material according to Example 16. To makethis construction, eight percent (8%) CMC solution was imbibed into asample of highly porous web material made according to Example 16 usinga roller to completely fill the void spaces of the highly porous webmaterial. The imbibed web was then dried under vacuum at 40° C. toproduce a CMC-imbibed high porosity, self-cohered, PGA:TMC web material.Upon immersion into PBS, the CMC swelled to produce a hydrogel-filledweb. Upon additional immersion for 10 min, the CMC dissolved and elutedfrom the web material.

Example 24

This example describes imbibing carboxymethylcellulose (CMC) intointerstitial spaces of a web material according to Example 21 andcross-linking the CMC to itself within the web material. To make thisconstruction, a finished material according to Example 21 was obtainedand subjected to chemical cross-linking as taught in U.S. Pat. No.3,379,720, issued to Reid, and incorporated herein by reference. In thisprocess, the pH of the four percent (4%) CMC solution was adjusted to pH4 with dropwise addition of thirty-seven percent (37%) HCl. Once the CMCwas imbibed and air dried according to Example 20, the composite wasplaced in an oven set at one hundred degrees centigrade (100° C.) forone (1) hour to induce ester crosslinks between carboxylic acid groupsand alcohol groups present on the CMC chemical backbone. The result wasa high porosity, self-cohered, stretched PGA:TMC web material with across-linked CMC material contained therein.

Example 25

This example describes swelling the cross-linked CMC web material ofExample 24 in PBS. The material of Example 24 was immersed into PBS forseveral minutes. Upon immersion, the CMC swelled to produce ahydrogel-filled web. Upon additional immersion for two (2) days, thecross-linked chemical groups of the CMC material caused the CMC to beretained within the web. Once filled with a cross-linked hydrogel, theweb material did not permit PBS to flow therethrough. The web materialof this embodiment functioned effectively as a fluid barrier.

Example 26

This example describes imbibing polyvinyl alcohol (PVA) intointerstitial spaces of a finished 7:1 web according to Example 5. Tomake this construction, USP grade polyvinyl alcohol (PVA) was obtainedfrom Spectrum Chemical Company, (Gardena, Calif.). The PVA was dissolvedin deionized water at a ten percent (10%) concentration (i.e., 10 g/100ml) using heat and stirring. Entrapped air was removed bycentrifugation. The PVA solution was imbibed into a web material (3.8cm×10.2 cm) according to Example 5 using a roller to completely fill thevoid spaces of the highly porous web. The imbibed web was air dried atroom temperature for sixteen hours (16 hrs) to produce a PVA-imbibed,self-cohered, PGA:TMC web material.

Example 27

This example describes imbibing polyvinyl alcohol (PVA) intointerstitial spaces of a web according to Example 26 and dissolving thePVA from the web into a phosphate buffer saline (PBS) solution. ThePVA-imbibed web material of Example 26 was immersed in a PBS solution.Upon immersion, the PVA swelled to produce a hydrogel-filled,self-cohered, stretched PGA:TMC web material. Upon immersion for anadditional ten (10) minutes, the PVA dissolved into the PBS and elutedfrom the web material.

Example 28

This example describes cross-linking a PVA-imbibed material according toExample 26 with succinic acid. Once PVA was imbibed into a web materialaccording to Example 26, the PVA was chemically cross-linked withsuccinic acid, a dicarboxylic acid, according to the teachings of U.S.Pat. No. 2,169,250, issued to Izard, and incorporated herein byreference.

PVA was dissolved in deionized water at a 10% concentration (i.e., 10g/100 ml) using heat and stirring. Succinic acid (Sigma) was alsodissolved in the PVA solution at a concentration of 2 g per 100 ml.Entrapped air was removed by centrifugation. The PVA-succinic acidsolution was imbibed into a 7:1 web material (3.8 cm×10.2 cm) accordingto Example 5 using a roller to completely fill the void spaces of thehighly porous web. The web material was air dried at room temperaturefor sixteen hours (16 hrs). The composite was placed in an oven set atone hundred forty degrees centigrade (140° C.) for fifteen (15) minutesto induce ester crosslinks between carboxylic acid groups present on thesuccinic acid and alcohol groups present on the PVA.

Example 29

This example describes cross-linking a PVA-imbibed material according toExample 26 with citric acid. Once PVA was imbibed into a web accordingto Example 26, the PVA was chemically crosslinked with citric acid, atricarboxylic acid, according to the teachings of U.S. Pat. No.2,169,250, issued to Izard, and incorporated herein by reference.

PVA was dissolved in deionized water at a 10% concentration (i.e., 10 gper 100 ml) using heat and stirring. Citric acid (Sigma) was alsodissolved in the PVA solution at a concentration of 2 g per 100 ml.Entrapped air was removed by centrifugation. The PVA-citric acidsolution was imbibed into a 7:1 web material (3.8 cm×10.2 cm) accordingto Example 5 using a roller to completely fill the void spaces of thehighly porous web material. The web material was air dried at roomtemperature for sixteen hours (16 hrs). The composite was placed in anoven set to one hundred forty degrees centigrade (140° C.) for fifteen(15) minutes to induce ester crosslinks between carboxylic acid groupspresent on the citric acid and alcohol groups present on the PVA.

Example 30

This example describes cross-linking a PVA-imbibed material according toExample 26 with aspartic acid. Once PVA was imbibed into a web accordingto Example 26, the PVA was chemically crosslinked with aspartic acid, adicarboxylic amino acid.

PVA was dissolved in deionized water at a 10% concentration (i.e., 10g/100 ml) using heat and stirring. Aspartic acid (free acid, Sigma) wasalso dissolved in the PVA solution at a concentration of 1 g per 100 ml.Entrapped air was removed by centrifugation. The PVA-aspartic acidsolution was imbibed into a 7:1 web material (3.8 cm×10.2 cm) accordingto Example 5 using a roller to completely fill the void spaces of thehighly porous web material. The web material was air dried at roomtemperature for sixteen hours (16 hrs). The composite was placed in anoven set to one hundred forty degrees centigrade (140° C.) for fifteen(15) minutes to induce ester crosslinks between carboxylic acid groupspresent on the aspartic acid and alcohol groups present on the PVA.

Example 31

This example describes cross-linking a PVA-imbibed material according toExample 26 with carboxymethylcellulose (CMC). Once PVA was imbibed intoa web according to Example 26, the PVA was chemically crosslinked withCMC, a polycarboxylic acid.

PVA was dissolved in deionized water at a 10% concentration (i.e., 10g/100 ml) using heat and stirring. CMC was also dissolved in the PVAsolution at a concentration of 1 g per 100 ml. In this process, the pHof the one percent (1%) CMC solution was adjusted to pH 1.5 withdropwise addition of thirty-seven percent (37%) HCl. Entrapped air wasremoved by centrifugation. The PVA-CMC acid solution was imbibed into a7:1 web material (3.8 cm×10.2 cm) according to Example 5 using a rollerto completely fill the void spaces of the highly porous web material.The web material was air dried at room temperature for sixteen hours (16hrs). The composite was placed in an oven set to one hundred fortydegrees centigrade (140° C.) for fifteen (15) minutes to induce estercrosslinks between carboxylic acid groups present on the CMC and alcoholgroups present on the PVA.

Example 32

This example describes swelling the hydrogel component of theconstructions of Examples 28-31 in PBS. Upon immersion of each of theseconstructions in a PBS solution, the PVA swelled to producehydrogel-filled web materials of the present invention. Upon additionalimmersion for two (2) days, the PVA was intact within all web materialsdue to the presence of the above-mentioned chemical cross-linkages. Eachhydrogel-filled web material was observed to prevent movement of PBSacross the web material.

Example 33

This example describes imbibing PLURONIC® surfactant into interstitialspaces of a web material according to Example 5. PLURONIC® surfactant isa copolymer of polyethylene glycol and polypropylene glycol, availablefrom BASF (Florham Park, N.J.). Certain grades of PLURONIC® surfactantform gels when immersed in warm biological fluids, such as grade F-127,as taught in U.S. Pat. No. 5,366,735, issued to Henry and incorporatedherein by reference. Grade F-127 PLURONIC® surfactant was dissolved indichloromethane at a concentration of 5 g per 5 ml.

The F-127 solution was imbibed into a 7:1 web material (3.8 cm×10.2 cm)according to Example 5 using a roller to completely fill the void spacesof the highly porous web material. The imbibed web material was dried atsixty degrees centigrade (60° C.) for five (5) minutes. The imbibed webmaterial was immersed in PBS, prewarmed to 37° C. Upon immersion, theF-127 swelled to produce a hydrogel-filled web material. Upon immersionfor an additional 1 day at 37° C., the F-127 dissolved and eluted fromthe web material.

Example 34

This example describes the incorporation of a bioactive species into thehydrogel material of a web material according to Example 21 (FIG. 9A).Dexamethasone (Sigma, St. Louis) was dissolved at a concentration of 10mg/100 ml in deionized water. Four grams of high viscosity CMC was addedto the solution using an industrial blender. Entrapped air was removedby centrifugation. The CMC/dexamethasone solution was imbibed into thefinished web using a roller, and was air dried at room temperature for16 hrs. Upon immersion into PBS, the CMC swells and the dexamethasonewas observed to elute from the hydrogel.

Example 35

This example describes the incorporation, with physical crosslinking, ofa bioactive species into the hydrogel material of a web materialaccording to Example 21. Dexamethasone phosphate (Sigma, St. Louis) wasdissolved at a concentration of 10 mg/100 ml in deionized water. Fourgrams of high viscosity CMC was added to the solution using anindustrial blender. Entrapped air was removed by centrifugation. TheCMC/dexamethasone phosphate solution was imbibed into the finished webusing a roller, and was air dried at room temperature for 16 hrs. Uponimmersion into PBS, the CMC swells and the dexamethasone phosphate wasobserved to elute from the hydrogel, at a rate slower than in Example34, due to physical acid/base complexation between the basicdexamethasone phosphate and the acidic CMC.

Example 36

This example describes the incorporation, with chemical crosslinking, ofa bioactive species into the hydrogel material of a web materialaccording to Example 24. Dexamethasone (Sigma, St. Louis) was dissolvedat a concentration of 10 mg/100 ml in deionized water. Four grams of CMCwas added to the solution using an industrial blender. The pH of thedexamethasone/CMC solution was adjusted to pH 4 with dropwise additionof thirty-seven percent (37%) HCl. Once the dexamethasone/CMC solutionwas imbibed and air dried according to Example 20, the composite wasplaced in an oven set at one hundred degrees centigrade (100° C.) forone (1) hour to induce ester crosslinks between carboxylic acid groupsand alcohol groups present on the CMC chemical backbone, and betweencarboxylic acid groups present on the CMC and alcohol groups present onthe dexamethasone. Upon immersion into PBS, the CMC swells and thedexamethasone was observed to elute from the hydrogel, at a rate slowerthan in Example 35, due to chemical ester-bond formation between thedexamethasone and the CMC.

Example 37

This example describes the incorporation, with chemical crosslinking, ofa bioactive species into the hydrogel material of a web materialaccording to Example 28. Dexamethasone (Sigma, St. Louis) was dissolvedat a concentration of 10 mg/100 ml in deionized water.

PVA was dissolved in the deionized water at a 10% concentration (i.e.,10 g/100 ml) using heat and stirring. Succinic acid (Sigma) was alsodissolved in the PVA solution at a concentration of 2 g per 100 ml.Entrapped air was removed by centrifugation. Thedexamethasone-PVA-succinic acid solution was then imbibed into a 7:1 webmaterial (3.8 cm×10.2 cm) according to Example 5 using a roller tocompletely fill the void spaces of the highly porous web. The webmaterial was air dried at room temperature for sixteen hours (16 hrs).The composite was placed in an oven set at one hundred forty degreescentigrade (140° C.) for fifteen (15) minutes to induce ester crosslinksbetween carboxylic acid groups present on the succinic acid and alcoholgroups present on the PVA, and between carboxylic acid groups present onthe succinic acid and alcohol groups present on the dexamethasone. Inthis manner, the dexamethasone was chemically linked via ester bonds tothe succinic acid, which in turn was chemically linked via ester bondsto the PVA. Upon immersion into PBS, the PVA swelled and thedexamethasone was observed to elute from the hydrogel at a slow rate,due to ester bond formation between the dexamethasone and the succinicacid/PVA.

Example 38

This example describes the formation of an article of the presentinvention to include an added material in combination with a stretchedbioabsorbable web. (FIG. 12).

A series of holes (0.5 cm) were cut in two rectangular pieces of solventcast film composed of 85% d,l-PLA-co-15% PGA copolymer (available fromAbsorbable Polymers, Pelham, Ala., USA). A similarly sized rectangularpiece of finished 6:1 web material according to Example 1 was obtainedand placed between the two pieces of the film material and pressedtogether at elevated temperature and time sufficient to provide for boththe softening and penetration of the PLA:PGA copolymer into theinterstices of the Example 1 web. The resulting laminate compositepossessed areas where the enclosed web material was regionally exposedby the film holes. Dependent on the applied pressure, temperature, andutilized film and web thicknesses, the porosity of the web between theopposing film layers may or may not become filled. Alternatively, thefilm, with or without holes, may be applied to a single surface of theprovided web. When exposed to aqueous conditions at 37° C., the filmcomponent imparts a malleable stiffness that facilitates the webconstruct's tactile manipulation and maintenance in a desired non-planarform prior to implantation.

The composition of the described laminate component or components may beselected from either absorbable or non-absorbable natural or syntheticmaterials with desirable properties that may additionally act ascarriers for bioactive agents, and may alternatively act as a mediaproviding a controlled rate of release of the contained bioactivesubstance or substances. The described laminate composite mayalternatively be affixed by various available means to other absorbableor non-absorbable natural or synthetic materials to elicit a biologicalresponse (e.g., heemostasis, inflammation), to provide for mechanicalsupport, and/or as a vehicle for delivery of bioactive agents.

Example 39

This example describes the construction of a composite materialcomprising a material of the present invention in combination with apledget material (FIG. 10). The material of the present invention aidsin holding the pledget material in place on a stapling apparatus duringa surgical procedure (FIGS. 10A and 10B).

Two finished porous 6:1 stretched self-cohered web materials accordingto Example 1 were obtained, cut into similarly sized rectangular shapeswith a pattern-following laser, and layered together to form a pouchbetween the layers. A pattern-following laser was also used to cut arectangular-shaped bioabsorbable pledget material made of a blockco-polymer of PGA:TMC (67:33 weight percent) obtained from W.L. Gore &Associates, Inc., Flagstaff, Ariz. The laser pattern controlled theexact dimensions of the three pieces of web material. The laser patternalso provided for four small alignment holes in the three pieces of webmaterial. The alignment holes were used to locate the individual pieceson a mandrel and assist in welding the web materials together. Themandrel had a square cross-sectional shape.

To construct the device, the two layered piece of porous stretched webmaterial was wrapped around three of the four sides of the mandrel andheld in place with locating pins placed through the laser-cut holes. Thepledget material was placed on the fourth side of the mandrel and heldin place with locating pins placed through the laser-cut holes. Once thepieces were properly juxtaposed, the combination was inserted onto anultrasonic welder and hot compression welds formed along the two longedges of the rectangular web materials to attach the porous stretchedweb material to the pledget material. The welds were approximately 0.025cm in width. The final form of the construction was generally tubular inshape with a substantially square cross-section. The ultrasonic weld wassufficiently strong to hold the pledget material on the staplingapparatus during manipulation of the pledget material, while remainingsufficiently frangible to allow the pledget material and the porousstretched web material to separate when a pulling force is applied tothe porous stretched web material.

To aid in separating the pledget material from the porous stretched webmaterial, a pull cord made of polyethylene terephthalate (PET) wasattached to the porous stretched web material prior to the above-recitedultrasonic welding process. A pull-tab was provided to the free end ofthe pull cord. Following construction of the composite material, theattached pull cord was coiled and stored in the pouch with the pull tabexposed.

In a similar embodiment, perforations were made in the pledget materialadjacent to the ultrasonic welds to aid in separating the pledgetmaterial from the porous stretched web material.

Example 40

This example describes the construction of a composite materialcomprising a material of the present invention in combination with anon-bioabsorbable material (FIG. 15). In this embodiment, thebioabsorbable material occupies an area distinct from thenon-bioabsorbable material of the composite. In particular, thiscomposite material of the present invention is useful as an implantabledental device where the non-bioabsorbable portion of the device canremain in the body of an implant recipient, while the bioabsorbableportion disappears from the body of the implant recipient in aforeseeable time period. In this embodiment, a second implantable dentaldevice can be placed in the area of the present invention originallyoccupied by the bioabsorbable portion of the invention.

A finished 6:1 web material according to Example 1 was obtained and cutinto an oval shape approximately 0.5 cm wide×0.75 cm long. A rectangularpiece of medical grade porous expanded polytetrafluoroethylene (ePTFE)with rounded corners was obtained from W.L. Gore & Associates, Inc.,Flagstaff, Ariz. The ePTFE material was 0.75 cm wide and 1.0 cm long. Ahole was cut in the ePTFE slightly smaller than the outer dimensions ofthe material of Example 1. The material of Example 1 was placed over thehole and solvent bonded in place using a small amount of aPLA:TMC/acetone solution applied along the edge of the hole sufficientto dissolve and flow some of the Example 1 material into the porousstructure of ePTFE material. The utilized acetone solution was composedof an approximately 20% (w/v) poly(70% lactide-co-30% trimethylenecarbonate), a copolymer commercially available from BoehringerIngelheim, (Ingelheim, Germany and Petersburg, Va., USA). The compositematerial was briefly placed in a heated oven below the melting point ofthe material of Example 1 and under reduced pressure to fully remove theacetone solvent from the implantable medical device.

The device of this example is particularly suited for medical situationsrequiring regrowth, or regeneration, of tissue at the site of defect orinjury. For example, in some dental applications, a space is created orenlarged in jawbone as part of a repair procedure. Unless surroundinggingival tissue is prevented from ingrowing the space, bone will notregrow in the space as desired. The device of this example is placedover the space in the bone to prevent unwanted tissues from ingrowingthe space, while regrowth of desired bone tissue is fostered. Withconventional devices made of ePTFE alone, the ePTFE remains permanentlyat the implantation site. In some situations, it may be desirable toplace a second implantable dental device, such as a metallic stud, inthe newly regrown bone tissue. Providing an ePTFE tissue barriermaterial with a bioabsorbable material according to the presentinvention would allow the bioabsorbable portion of the device todisappear from the implantation site and leave an unobstructed paththrough the ePTFE material to place a second dental implant.

Example 41

This example describes the construction of a composite material of thepresent invention having a non-bioabsorbable component combined with abioabsorbable component (FIG. 21). In this example, a finished 6:1bioabsorbable web material as described in Example 1 is bonded to aporous expanded polytetrafluoroethylene material to form an implantablesheet. The sheet can be used as a replacement, or substitute, for avariety of anatomical membranes. In particular, these membranes areuseful as substitutes for dura and other membranes of the nervoussystem.

A bioabsorbable material according to Example 1 was obtained andoverlaid on a thin ePTFE sheet material having delicate fibrils andspacious pore volumes. The ePTFE material was made according to U.S.Pat. No. 5,476,589 issued to Bacino, which is incorporated herein byreference.

The two sheets of material were solvent bonded together using thepreviously described PLA:TMC/acetone solution. Once bonded, the acetonewas removed under heat and vacuum. The result was a composite sheetmaterial suitable for use as an implantable medical device.

Example 42

This example describes the use of a porous, self-cohered, stretched webmaterial of the present invention as an external supportive wrap for ananatomical structure or organ (FIG. 11). The wrap can also be used at ananastomotic site to minimize leakage and tissue adhesions.

In this example, a tissue compatibility study was performed in a groupof animals. In the study, a piece of a porous, self-cohered, stretchedweb material made according to Example 1 was cut into a rectangularpiece 2 cm×5 cm. The finished uni-axially 6:1 stretched web material ofExample 1 exhibited an ability to elongate in the longer dimension ofthe web (i.e., 10 cm). A control material made from non-bioabsorbablematerials was obtained from W.L. Gore & Associates, Inc., Flagstaff,Ariz. under the tradename PRECLUDE® Dura Substitute (PDS).

Two sites on each colon of eight (8) New Zealand White rabbits were usedfor the tests. At a distal site approximately 5 cm from the anus, apiece of one of the test materials was wrapped around the colon. Fivecentimeters further up the colon, more proximal, another piece of testmaterial, different from the first piece, was wrapped around the colon.The materials formed sleeves around the serosa of the colon and weretacked in place with GORE-TEX® Sutures.

At the end of seven (7) days and thirty (30) days, all of the animalswere sacrificed and the various materials retrieved intact. Theparticular segment of the wrapped colon with any accompanying adhesionswere immersed in 10% neutral buffered formalin for paraffin histology.Adhesions to the materials were scored.

Upon gross evaluation and histologic analysis of the web material of thepresent invention showed incorporation of the web material in the serosaat seven (7) days. The web material of the present invention was wellincorporated to the serosa of the colon as well as to the surroundingadhesions day thirty-one (31). The web material of the present inventionwas seen to be highly vascularized at both seven (7) and thirty-one (31)days. The PDS was not incorporated into the serosa at seven (7) orthirty-one (31) days nor had the material become vascularized.

The use of a web material of the present invention in combination with acoating of a bioabsorbable adhesion barrier material such as partiallycrosslinked polyvinyl alcohol (PVA), carboxymethylcellulose orhyaluronic acid biomaterial might be advantageous.

1. An implantable article in the form of a hollow tube comprisingmelt-formed continuous filaments intermingled to form a porous webwherein said filaments are self-cohered to each other at multiplecontact points, wherein said filaments comprise at least onesemi-crystalline polymeric component covalently bonded to or blendedwith at least one amorphous polymeric component, wherein said filamentspossess partial to full polymeric component phase immiscibility when ina crystalline state, wherein said filaments have a mean diameter of fromsixteen (16) to twenty (20) microns, and wherein said porous web has apercent porosity greater than ninety.
 2. The implantable article ofclaim 1 further comprising a framework attached to said hollow tube. 3.The implantable article of claim 2 wherein said framework is a metallicmaterial.
 4. The implantable article of claim 2 wherein said frameworkis made of a bioabsorbable material.
 5. The implantable article of claim1 wherein the percent porosity is greater than ninety-one.
 6. Theimplantable article of claim 5 further comprising a framework attachedto said hollow tube.
 7. The implantable article of claim 6 wherein saidframework is a metallic material.
 8. The implantable article of claim 7wherein said framework is a bioabsorbable material.
 9. The implantablearticle of claim 1 wherein the at least one semi-crystalline polymericcomponent is covalently bonded to at least one amorphous polymericcomponent.
 10. The implantable article of claim 9 wherein the componentscomprise a block copolymer.
 11. The implantable article of claim 1wherein the at least one semi-crystalline polymeric component is blendedwith the at least one amorphous polymeric component.
 12. The implantablearticle of claim 11 wherein at least one of the components is a blockco-polymer.
 13. The implantable article of claim 1 wherein at least onesemi-crystalline polymeric component has a melting point greater thaneighty degrees centigrade (80° C.).
 14. An implantable article in theform of a hollow tube comprising melt-formed continuous filamentsintermingled to form a porous web wherein said filaments areself-cohered to each other at multiple contact points, wherein saidfilaments comprise a first semi-crystalline polymeric componentcovalently bonded to or blended with at least one additionalsemi-crystalline polymeric component, wherein said filaments possesspartial to full polymeric component phase immiscibility when in acrystalline state, wherein said filaments have a mean diameter of fromsixteen (16) to twenty (20) microns, and wherein said porous web has apercent porosity greater than ninety.
 15. The implantable article ofclaim 14 wherein said implantable article has a percent porosity greaterthan ninety-one.
 16. The implantable article of claim 15 wherein saidframework is a metallic material.
 17. The implantable article of claim15 wherein said framework is made of a bioabsorbable material.
 18. Theimplantable article of claim 14 further comprising a framework attachedto said hollow tube.
 19. The implantable article of claim 14 wherein thepercent porosity is greater than ninety-one.
 20. The implantable articleof claim 19 further comprising a framework attached to said hollow tube.21. The implantable article of claim 20 wherein said framework is ametallic material.
 22. The implantable article of claim 21 wherein saidframework is a bioabsorbable material.
 23. The implantable article ofclaim 14 wherein the at least one semi-crystalline polymeric componentis covalently bonded to at least one amorphous polymeric component. 24.The implantable article of claim 23 wherein the components comprise ablock copolymer.
 25. The implantable article of claim 14 wherein the atleast one semi-crystalline polymeric component is blended with the atleast one amorphous polymeric component.
 26. The implantable article ofclaim 25 wherein at least one of the components is a block co-polymer.27. The implantable article of claim 14 wherein at least onesemi-crystalline polymeric component has a melting point greater thaneighty degrees centigrade (80° C.).
 28. An implantable articlecomprising melt-formed continuous filaments intermingled to form aporous web wherein said filaments are self-cohered to each other atmultiple contact points, wherein said filaments comprise at least onesemi-crystalline polymeric component covalently bonded to or blendedwith at least one amorphous polymeric component, wherein said filamentspossess partial to full polymeric component phase immiscibility when ina crystalline state, wherein said filaments have a mean diameter of fromsixteen (16) to twenty (20) microns, wherein said porous web has apercent porosity greater than ninety, and wherein said porous web is inthe form of a corrugated tube capable of increasing in length anddiameter.
 29. The implantable article of claim 28 wherein the percentporosity is greater than ninety-one.
 30. The implantable article ofclaim 28 wherein the at least one semi-crystalline polymeric componentis covalently bonded to at least one amorphous polymeric component. 31.The implantable article of claim 30 wherein the components comprise ablock copolymer.
 32. The implantable article of claim 28 wherein the atleast one semi-crystalline polymeric component is blended with the atleast one amorphous polymeric component.
 33. The implantable article ofclaim 32 wherein at least one of the components is a block co-polymer.34. The implantable article of claim 28 wherein at least onesemi-crystalline polymeric component has a melting point greater thaneighty degrees centigrade (80° C.).